Minimum Order Quantity | 200 Kg |
Application | Automobile Industry |
Shape | Square |
Single Piece Length | 6 meter |
Hardness HB | Max 230 |
Hardening Degree C | 1000-1030 |
Hardness after quenching HRC | 54 |
Cooling | Furnace |
Length | 3 - 18 Meter |
We are offering 2343 Die Steel Square Bars to our clients.
Chemical Composition - (Typical Analysis in %)
STANDARDS | X37CrMoV5 | H11 | DIN 2343 | AISI H11 | AFNOR Z38CDV5 | JIS SKD6 |
C | Si | Mn | P | S | Cr | Mo | V |
0.33-0.41 | 0.80-1.00 | 0.25-0.50 | 0.003 max | 0.030max | 4.80-5.50 | 1.10-1.50 | 0.30-0.50 |
USA | Europe | Germany | China | Japan | India | R. of Korea | Russia |
AISI / SAE | En | DIN, WNr | GB | JIS | IS | KS | GOST |
H11 | X37CrMoV5-1 | X38CrMoV5-1 | 4Cr5MoSiV | SKD6 | XT35Cr5Mo1V3 | STD 6 | 4Ch5MFS |
Ventura Alloy and Steels Supplies and Stocks AISI H11 tool steel is a 5% chromium hot work tool steel that is represented by its excellent impact toughness. The most commonly used chromium hot-work steels are H11 tool steel, H12 tool steel, and H13 steel, within the series from H1 to H19.
If we compare between H11 and H13, H11 tool steel consists of less vanadium than the commonly used H13 hot work tool steel. That gives minimal size change during heat treatment. H11 how work steel also has super resistance to thermal fatigue cracking and superb resistance to gross cracking and thermal shock when water cooled in service.
H11 steel is inclusive of all hot work tool steel with excellent rigidity and durability along with great thermal conductivity and invulnerability to hot cracking and can be water cooled to a constrained degree. H11 is primarily used for apparatus holders , ejector pins and shrink fit chucks.
Steel Properties:
Application:
This grade isn't utilized for typical applications in the area of hot-work steels, yet additionally useful for tool holders, bridge kind tools, ejector pins, liner holders, hot work punches, forging dies, and shrink work chucks.
Minimum Order Quantity | 200 Kg |
Application | Automobile Industry |
Single Piece Length | 6 meter |
Material | Alloy Steel |
Shape | Square |
Technique | Hot Rolled |
Hardness HB | Max 230 |
Hardening Degree C | 1000-1030 |
Hardness after quenching HRC | 54 |
Cooling | Furnace |
Length | 3 - 18 Meter |
We are offering 1.2343 Die Steel Square Bar to our clients.
Chemical Composition - (Typical Analysis in %)
STANDARDS | X37CrMoV5 | H11 | DIN 2343 | AISI H11 | AFNOR Z38CDV5 | JIS SKD6 |
C | Si | Mn | P | S | Cr | Mo | V |
0.33-0.41 | 0.80-1.00 | 0.25-0.50 | 0.003 max | 0.030max | 4.80-5.50 | 1.10-1.50 | 0.30-0.50 |
USA | Europe | Germany | China | Japan | India | R. of Korea | Russia |
AISI / SAE | En | DIN, WNr | GB | JIS | IS | KS | GOST |
H11 | X37CrMoV5-1 | X38CrMoV5-1 | 4Cr5MoSiV | SKD6 | XT35Cr5Mo1V3 | STD 6 | 4Ch5MFS |
Ventura Alloy and Steels Supplies and Stocks AISI H11 tool steel is a 5% chromium hot work tool steel that is represented by its excellent impact toughness. The most commonly used chromium hot-work steels are H11 tool steel, H12 tool steel, and H13 steel, within the series from H1 to H19.
If we compare between H11 and H13, H11 tool steel consists of less vanadium than the commonly used H13 hot work tool steel. This gives H11 steels the higher toughness, with some reduction in wear resistance and tamper resistance. That gives minimal size change during heat treatment. H11 how to work steel also has super resistance to thermal fatigue cracking and superb resistance to gross cracking and thermal shock when water cooled in service.
H11 steel is inclusive of all hot work tool steel with excellent rigidity and durability along with great thermal conductivity and invulnerability to hot cracking and can be water cooled to a constrained degree. H11 is primarily used for apparatus holders , ejector pins and shrink fit chucks.
Steel Properties:
Application:
This grade isn't utilized for typical applications in the area of hot-work steels, yet additionally useful for tool holders, bridge kind tools, ejector pins, liner holders, hot work punches, forging dies, and shrink work chucks.
Minimum Order Quantity | 200 Kg |
Material | Alloy Steel |
Application | Extrusion |
Shape | Square |
Hardness HB | Max 240 |
Hardening Degree C | 1000-1130 |
Hardness after quenching HRC | 53 |
Cooling | Slowly |
Soft annealing Degree C | 780-810 |
Coefficient of thermal expansionat Degree C | 20-700 |
Quenching | Oil or Hot Bath,600-650 degree C |
Length | 3 - 18 Meter |
Chemical Composition - (Typical Analysis in %)
STANDARDS |
X30WCrV-3 |
H21 |
DIN 2581 |
AISI H21 |
AFNOR 32CDV12-28 |
JIS SKD5 |
C |
Si |
Mn |
P |
S |
Cr |
W |
V |
0.26-0.36 |
0.15-0.25 |
0.20-0.40 |
0.003 max |
0.030max |
3.00-3.75 |
8.50-10.00 |
0.30-0.60 |
USA |
France |
Germany |
China |
Japan |
England |
Sweden |
AISI / SAE |
AFNOR |
DIN, WNr |
GB |
JIS |
BS |
|
H21 / T20821 |
X30WCrV9 |
X30WCrV93 / 1.2581 |
3Cr2W8V |
SKD5 |
BH21 |
2730 |
H21 Steel is a hot work tool steel for oil or air hardening to develop high hot quality, support of hardness, and warmth checking resistance.
This is mostly utilized as hot work devices, instruments for manufacture of hollows, screws, rivets, nuts and bolts. Die casting tools, forming dies, die inserts, hot shear blades.
Steel Properties:
Hot work steel has great toughness and contains Tungsten, Chromium, Carbon, Vanadium and generally its working hardness is 40.0 to 55.0 HRC size and is accessible in round, level and square shapes.
Application:
The H21 tungsten hot-work tool steels are primarily utilized for hot-working dies and tooling. For example extrusion, die casting & hot-forming of parts.
Physical Properties:
Coefficient of Thermal Expansion at °C |
10¯??? m / (m*K) |
20-100 |
11.2 |
20-200 |
11.9 |
20-300 |
12.2 |
20-400 |
12.5 |
20-500 |
12.8 |
20-600 |
13.0 |
20-700 |
13.2 |
Thermal Conductivity at °C |
W / (m*K) |
100 |
27.0 |
400 |
29.8 |
675 |
29.1 |
Tempering°C after quenching |
100 |
210 |
300 |
400 |
500 |
550 |
600 |
650 |
700 |
HRC |
49 |
49 |
49 |
49 |
51 |
51 |
50 |
46 |
36 |