Minimum Order Quantity | 200 Kg |
Usage/Application | Construction |
Single Piece Length | 3 - 18 Meter |
Technique | Hot Rolled |
Shape | Rounds |
Thickness/Diameter | 10 - 500 mm |
Material | SS |
Hardness HB | max 240 |
Hardening Degree C | 1030-1060 Deg C |
Hardness after quenching HRC | 55 HRC |
Cooling | Furnace |
Soft annealing Degree C | 760 - 810 Deg C |
Thermal Conductivity Degree C | 20-700 Deg C |
Chemical Composition - (Typical Analysis in %)
STANDARDS | X40CrMoV5 | H13 | DIN 2344 | AISI H13 | AFNOR Z40CDV5 | JIS SKD61 |
C | Si | Mn | P | S | Cr | Mo | V |
0.35-0.45 | 0.90-1.20 | 0.30-0.50 | <0.03 | <0.004 | 4.90-5.40 | 1.20-1.75 | 0.90-1.20 |
Ventura Alloy and Steels supplies and stocks H13 tool steel in flat, square and round bar. We provide steel in all sizes as your requirements. Consult our team who will assist you for any query related to H13 steel.
SAE AISI H13 steel equivalent with JIS SKD61, GB 4Cr5MoSiV1 and DIN 1.2344 Tool Steel. AISI H13 steel consists of chromium, molybdenum and vanadium and is known for its high hardenability and great toughness.
The molybdenum and vanadium act as strengthening agents while the chromium content helps the AISI H-13 tool steel to withstand softening when used at high temperatures. It also combines shock and abrasion resistance, has good red hardness, can resist rapid cooling and withstand premature heat checking.
H13 Tool Steel has high hot-wear resistance abilities along with great strength, heat conductivity and invulnerability to hot cracking. It has good resistance to abrasion at each low and high temperature. It displays high level of toughness and ductility. H13 has Uniform and high level of machinability and polish ability. It has high-temperature strength and resistance to thermal fatigue, glorious through-hardening properties and shows very limited distortion during hardening.
H3 ESR is the most purified material with the conventional VD route. The nature of material increase the strength, exceptionally increase the micro-cleanness level. H13 ESR is most refined, has greater homogeneity and an exceptionally fine structure, resulting in improved machinability, polishing & high temperature tensile strength. Exceptionally suggest the use of AISI-H13 ESR grade for Aluminum Pressure Die Casting and other part subjected to high working temperatures and high weight quality. H13 is completely ultrasonic examined with 100% positive outcomes according to NDT standards.
Steel Properties:
Great toughness
Thermal conductivity
High hot-wear resistance
Hot tensile strength
Insusceptible for hot cracking (Hot Crack resistant)
Can be water-cooled to a restricted degree
High Hardenability
Application:
This steel is especially used for ejector pins, tool holders and shrink work chucks. It is majorly widely utilized for manufacture of hot forging die & inserts, hot gripper dies, hot nut tools, hot header dies, brass forging and pressing dies, hot forging aluminum base dies, aluminum casting and extrusion dies, zinc die casting dies, extrusion mandrels, cores, die holder blocks, hot press dies, hot work punches, etc.
Minimum Order Quantity | 200 Onwards |
Usage/Application | Construction |
Single Piece Length | 6 meter |
Technique | Hot Rolled |
Shape | Rounds |
Thickness/Diameter | 10 - 500 mm |
Hardness HB | Max 240 |
Hardening Degree C | 1030-1060 Deg C |
Hardness after quenching HRC | 55 HRC |
Cooling | Furnace |
Soft annealing Degree C | 760 - 810 Deg C |
Thermal Conductivity Degree C | 20-700 Deg C |
Chemical Composition - (Typical Analysis in %)
STANDARDS | X40CrMoV5 | H13 | DIN 2344 | AISI H13 | AFNOR Z40CDV5 | JIS SKD61 |
C | Si | Mn | P | S | Cr | Mo | V |
0.35-0.45 | 0.90-1.20 | 0.30-0.50 | <0.03 | <0.004 | 4.90-5.40 | 1.20-1.75 | 0.90-1.20 |
Ventura Alloy and Steels supplies and stocks H13 tool steel in flat, square and round bar. We provide steel in all sizes as your requirements. Consult our team who will assist you for any query related to H13 steel.
SAE AISI H13 steel equivalent with JIS SKD61, GB 4Cr5MoSiV1 and DIN 1.2344 Tool Steel. AISI H13 steel consists of chromium, molybdenum and vanadium and is known for its high hardenability and great toughness.
The molybdenum and vanadium act as strengthening agents while the chromium content helps the AISI H-13 tool steel to withstand softening when used at high temperatures. It also combines shock and abrasion resistance, has good red hardness, can resist rapid cooling and withstand premature heat checking.
H13 Tool Steel has high hot-wear resistance abilities along with great strength, heat conductivity and invulnerability to hot cracking. It has good resistance to abrasion at each low and high temperature. It displays high level of toughness and ductility. H13 has Uniform and high level of machinability and polish ability. It has high-temperature strength and resistance to thermal fatigue, glorious through-hardening properties and shows very limited distortion during hardening.
H3 ESR is the most purified material with the conventional VD route. The nature of material increase the strength, exceptionally increase the micro-cleanness level. H13 ESR is most refined, has greater homogeneity and an exceptionally fine structure, resulting in improved machinability, polishing & high temperature tensile strength. Exceptionally suggest the use of AISI-H13 ESR grade for Aluminum Pressure Die Casting and other part subjected to high working temperatures and high weight quality. H13 is completely ultrasonic examined with 100% positive outcomes according to NDT standards.
Steel Properties:
Great toughness
Thermal conductivity
High hot-wear resistance
Hot tensile strength
Insusceptible for hot cracking (Hot Crack resistant)
Can be water-cooled to a restricted degree
High Hardenability
Application:
This steel is especially used for ejector pins, tool holders and shrink work chucks. It is majorly widely utilized for manufacture of hot forging die & inserts, hot gripper dies, hot nut tools, hot header dies, brass forging and pressing dies, hot forging aluminum base dies, aluminum casting and extrusion dies, zinc die casting dies, extrusion mandrels, cores, die holder blocks, hot press dies, hot work punches, etc.
Minimum Order Quantity | 200 KG |
Single Piece Length | 3 - 18 Meter |
Usage/Application | Construction |
Shape | Round |
Surface Finish | Polished |
Material | Alloy Steel |
Thickness/Diameter | 6 - 450 mm Dia. |
Standard | Grade | C | Mn | P | S | Si | Ni | Cr | Mo |
ASTM A29 | 4340 | 0.38-0.43 | 0.60-0.80 | 0.035 max | 0.040 max | 0.15-0.35 | 1.65-2.00 | 0.70-0.90 | 0.20-0.30 |
EN 10250 | 36CrNiMo4 / 1.6511 | 0.32-0.40 | 0.50-0.80 | 0.035 max | 0.035 max | 0.40 max | 0.90-1.20 | 0.90-1.2 | 0.15-0.30 |
BS 970 | EN24 / 817M40 | 0.36-0.44 | 0.45-0.70 | 0.035 max | 0.040 max | 0.10-0.40 | 1.30-1.70 | 1.00-1.40 | 0.20-0.35 |
JIS G4103 | SNCM 439 / SNCM 8 | 0.36-0.43 | 0.60-0.90 | 0.035 max | 0.030 max | 0.15-0.35 | 1.60-2.00 | 0.60-1.00 | 0.15-0.30 |
Thermal Conductivity at °C | W / (m*K) |
20 | 40.5 |
350 | 32.5 |
700 | 25.5 |
Soft Annealing °C | 650-700 |
Cooling | Slowly |
Hardness HB | max. 280 |
Stress-relief Annealing °C | 630-650 |
Cooling | Furnace |
1st Pre-Heating °C | up to approx. 400 in an air-circulating furnace |
2nd and 3rd | 780 and 1000 |
Hardening °C | 1190-1230 |
Quenching | Salt Bath, at least 520°C Oil, Air |
Tempering °C | at least twice 530-560 |
Hardness after Temperature HRC | 64-66 |
Minimum Order Quantity | 200 Kilogram |
Single Piece Length | 3 - 18 Meter |
Usage/Application | Construction |
Shape | Round |
Surface Finish | Polished |
Material | Alloy Steel |
Thickness/Diameter | 6 to 450 mm Dia. |
Standard | Grade | C | Mn | P | S | Si | Ni | Cr | Mo |
ASTM A29 | 4340 | 0.38-0.43 | 0.60-0.80 | 0.035 max | 0.040 max | 0.15-0.35 | 1.65-2.00 | 0.70-0.90 | 0.20-0.30 |
EN 10250 | 36CrNiMo4 / 1.6511 | 0.32-0.40 | 0.50-0.80 | 0.035 max | 0.035 max | 0.40 max | 0.90-1.20 | 0.90-1.2 | 0.15-0.30 |
BS 970 | EN24 / 817M40 | 0.36-0.44 | 0.45-0.70 | 0.035 max | 0.040 max | 0.10-0.40 | 1.30-1.70 | 1.00-1.40 | 0.20-0.35 |
JIS G4103 | SNCM 439 / SNCM 8 | 0.36-0.43 | 0.60-0.90 | 0.035 max | 0.030 max | 0.15-0.35 | 1.60-2.00 | 0.60-1.00 | 0.15-0.30 |
Thermal Conductivity at °C | W / (m*K) |
20 | 40.5 |
350 | 32.5 |
700 | 25.5 |
Soft Annealing °C | 650-700 |
Cooling | Slowly |
Hardness HB | max. 280 |
Stress-relief Annealing °C | 630-650 |
Cooling | Furnace |
1st Pre-Heating °C | up to approx. 400 in an air-circulating furnace |
2nd and 3rd | 780 and 1000 |
Hardening °C | 1190-1230 |
Quenching | Salt Bath, at least 520°C Oil, Air |
Tempering °C | at least twice 530-560 |
Hardness after Temperature HRC | 64-66 |
Usage/Application | As Per Requirement |
Thickness | As per requirement |
Grade | As per requirement |
Material | As per requirement |
Brand | As per requirement |
Carbon | As per requirement |
Current | As per requirement |
Diameter | As per requirement |
Elongation | As per requirement |
Imperial | As per requirement |
Minimum Order Quantity | 200 Kg |
Single Piece Length | 3 - 18 Meter |
Application | Automobile Industry |
Shape | Rounds |
Hardness HB | Max 230 |
Hardening Degree C | 1000-1030 Deg C |
Hardness after quenching HRC | 54 HRC |
Cooling | Furnace |
Soft annealing Degree C | 750 - 800 Deg C |
Coefficient of thermal expansionat Degree C | 20-700 Deg C |
Stress relief annealing Degree C | Approx 600 - 650 Deg C |
Diameter | 71 - 300 mm |
We are offering SKD6 SS Round Rods to our clients.
Chemical Composition - (Typical Analysis in %)
STANDARDS | X37CrMoV5 | H11 | DIN 2343 | AISI H11 | AFNOR Z38CDV5 | JIS SKD6 |
C | Si | Mn | P | S | Cr | Mo | V |
0.33-0.41 | 0.80-1.00 | 0.25-0.50 | 0.003 max | 0.030max | 4.80-5.50 | 1.10-1.50 | 0.30-0.50 |
USA | Europe | Germany | China | Japan | India | R. of Korea | Russia |
AISI / SAE | En | DIN, WNr | GB | JIS | IS | KS | GOST |
H11 | X37CrMoV5-1 | X38CrMoV5-1 | 4Cr5MoSiV | SKD6 | XT35Cr5Mo1V3 | STD 6 | 4Ch5MFS |
Ventura Alloy and Steels Supplies and Stocks AISI H11 tool steel is a 5% chromium hot work tool steel that is represented by its excellent impact toughness. Chromium hot-work tool steels are designated as group H steels according to the AISI classification system, and specified in ASTM A681 standard. The most commonly used chromium hot-work steels are H11 tool steel, H12 tool steel, and H13 steel, within the series from H1 to H19.
If we compare between H11 and H13, H11 tool steel consists of less vanadium than the commonly used H13 hot work tool steel. This gives H11 steels the higher toughness. That gives minimal size change during heat treatment. H11 how work steel also has super resistance to thermal fatigue cracking and superb resistance to gross cracking and thermal shock when water cooled in service.
H11 steel is inclusive of all hot work tool steel with excellent rigidity and durability along with great thermal conductivity and invulnerability to hot cracking and can be water cooled to a constrained degree. H11 is primarily used for apparatus holders , ejector pins and shrink fit chucks.
Steel Properties:
Application:
This grade isn't utilized for typical applications in the area of hot-work steels, yet additionally useful for tool holders, bridge kind tools, ejector pins, liner holders, hot work punches, forging dies, and shrink work chucks.
Minimum Order Quantity | 200 Onwards |
Single Piece Length | 3 - 18 Meter |
Technique | Hot Rolled |
Length | 3 - 18 Meter |
Material | Spring Steel |
Shape | Rounds |
Application | Automobile Industry, Construction |
Thickness/Diameter | 10 - 500 mm |
Hardening degree C | 1030 - 1060 Deg C |
Quenching | Air,Oil or Saltbath,500 - 550 Degree C |
Cooling | Furnace |
Hardness HB | Max 240 |
Coefficient of thermal expansionat Degree C | 20-700 Deg C |
Thermal Conductivity Degree C | 20-700 Deg C |
Soft annealing Degree C | 760 - 810 Deg C |
Hardness after quenching HRC | 55 HRC |
Stress Relief Annealing Degree C | Approx. 610-660 Deg C |
We are offering SKD61 Hot Work Steel Rods to our clients.
Chemical Composition - (Typical Analysis in %)
STANDARDS |
X40CrMoV5 |
H13 |
DIN 2344 |
AISI H13 |
AFNOR Z40CDV5 |
JIS SKD61 |
C |
Si |
Mn |
P |
S |
Cr |
Mo |
V |
0.35-0.45 |
0.90-1.20 |
0.30-0.50 |
<0.03 |
<0.004 |
4.90-5.40 |
1.20-1.75 |
0.90-1.20 |
Ventura Alloy and Steels supplies and stocks H13 tool steel in flat, square and round bar. We provide steel in all sizes as your requirements. Consult our team who will assist you for any query related to H13 steel.
SAE AISI H13 steel equivalent with JIS SKD61, GB 4Cr5MoSiV1 and DIN 1.2344 Tool Steel. AISI H13 steel consists of chromium, molybdenum and vanadium and is known for its high hardenability and great toughness.
The molybdenum and vanadium act as strengthening agents while the chromium content helps the AISI H-13 tool steel to withstand softening when used at high temperatures.
H13 Tool Steel has high hot-wear resistance abilities along with great strength, heat conductivity and invulnerability to hot cracking. It displays high level of toughness and ductility. H13 has Uniform and high level of machinability and polish ability. It has high-temperature strength and resistance to thermal fatigue, glorious through-hardening properties and shows very limited distortion during hardening.
H3 ESR is the most purified material with the conventional VD route. The nature of material increase the strength, exceptionally increase the micro-cleanness level. Exceptionally suggest the use of AISI-H13 ESR grade for Aluminum Pressure Die Casting and other part subjected to high working temperatures and high weight quality. H13 is completely ultrasonic examined with 100% positive outcomes according to NDT standards.
Steel Properties:
Application:
This steel is especially used for ejector pins, tool holders and shrink work chucks. It is majorly widely utilized for manufacture of hot forging die & inserts, hot gripper dies, hot nut tools, hot header dies, brass forging and pressing dies, hot forging aluminum base dies, aluminum casting and extrusion dies, zinc die casting dies, extrusion mandrels, cores, die holder blocks, hot press dies, hot work punches, etc.
Minimum Order Quantity | 200 Kg |
Application | Automobile Industry |
Single Piece Length | 6 meter |
Shape | Round |
Hardness HB | max 230 |
Hardening Degree C | 1000-1030 Deg C |
Hardness after quenching HRC | 54 HRC |
Cooling | Furnace |
Diameter | 71 - 300 mm |
Length | 3 - 18 Meter |
Chemical Composition - (Typical Analysis in %)
STANDARDS | X37CrMoV5 | H11 | DIN 2343 | AISI H11 | AFNOR Z38CDV5 | JIS SKD6 |
C | Si | Mn | P | S | Cr | Mo | V |
0.33-0.41 | 0.80-1.00 | 0.25-0.50 | 0.003 max | 0.030max | 4.80-5.50 | 1.10-1.50 | 0.30-0.50 |
USA | Europe | Germany | China | Japan | India | R. of Korea | Russia |
AISI / SAE | En | DIN, WNr | GB | JIS | IS | KS | GOST |
H11 | X37CrMoV5-1 | X38CrMoV5-1 | 4Cr5MoSiV | SKD6 | XT35Cr5Mo1V3 | STD 6 | 4Ch5MFS |
Ventura Alloy and Steels Supplies and Stocks AISI H11 tool steel is a 5% chromium hot work tool steel that is represented by its excellent impact toughness. Chromium hot-work tool steels are designated as group H steels according to the AISI classification system, and specified in ASTM A681 standard. The most commonly used chromium hot-work steels are H11 tool steel, H12 tool steel, and H13 steel, within the series from H1 to H19.
If we compare between H11 and H13, H11 tool steel consists of less vanadium than the commonly used H13 hot work tool steel. This gives H11 steels the higher toughness, with some reduction in wear resistance and tamper resistance. H11 tool steel is a deep-hardening, air-hardening steel and H11 alloy steel could be deep hardened by heat treatment and air-quenching. That gives minimal size change during heat treatment. H11 how work steel also has super resistance to thermal fatigue cracking and superb resistance to gross cracking and thermal shock when water cooled in service.
H11 steel is inclusive of all hot work tool steel with excellent rigidity and durability along with great thermal conductivity and invulnerability to hot cracking and can be water cooled to a constrained degree. H11 is primarily used for apparatus holders , ejector pins and shrink fit chucks.
Steel Properties:
Contains 5% Chromium
Greater strength
High toughness
Best thermal physical phenomenon
Resistant to hot cracking
Gives fundamental necessities to long tool life in press forging, die-casting, extrusion processes etc.
Application:
This grade isn't utilized for typical applications in the area of hot-work steels, yet additionally useful for tool holders, bridge kind tools, ejector pins, liner holders, hot work punches, forging dies, and shrink work chucks.
Minimum Order Quantity | 200 Kg |
Application | Automobile Industry |
Single Piece Length | 3 - 18 Meter |
Material | Alloy Steel |
Shape | Round |
Hardness HB | Max 240 |
Hardening Degree C | 1030-1060 Deg C |
Hardness after quenching HRC | 55 HRC |
Cooling | Furnace |
Soft annealing Degree C | 760 - 810 Deg C |
Thermal Conductivity Degree C | 20-700 Deg C |
Diameter | 10 to 500 mm |
We are offering X40CRMOV5-1 Die Steel Round Bar to our clients.
Chemical Composition - (Typical Analysis in %)
STANDARDS | X40CrMoV5 | H13 | DIN 2344 | AISI H13 | AFNOR Z40CDV5 | JIS SKD61 |
C | Si | Mn | P | S | Cr | Mo | V |
0.35-0.45 | 0.90-1.20 | 0.30-0.50 | <0.03 | <0.004 | 4.90-5.40 | 1.20-1.75 | 0.90-1.20 |
Ventura Alloy and Steels supplies and stocks H13 tool steel in flat, square and round bar. We provide steel in all sizes as your requirements. Consult our team who will assist you for any query related to H13 steel.
SAE AISI H13 steel equivalent with JIS SKD61, GB 4Cr5MoSiV1 and DIN 1.2344 Tool Steel. AISI H13 steel consists of chromium, molybdenum and vanadium and is known for its high hardenability and great toughness.
The molybdenum and vanadium act as strengthening agents while the chromium content helps the AISI H-13 tool steel to withstand softening when used at high temperatures.
H13 Tool Steel has high hot-wear resistance abilities along with great strength, heat conductivity and invulnerability to hot cracking. It has good resistance to abrasion at each low and high temperature. It displays high level of toughness and ductility. H13 has Uniform and high level of machinability and polish ability. It has high-temperature strength and resistance to thermal fatigue, glorious through-hardening properties and shows very limited distortion during hardening.
H3 ESR is the most purified material with the conventional VD route. The nature of material increase the strength, exceptionally increase the micro-cleanness level. Exceptionally suggest the use of AISI-H13 ESR grade Aluminum Pressure Die Casting and other part subjected to high working temperatures and high weight quality. H13 is completely ultrasonic examined with 100% positive outcomes according to NDT standards.
Steel Properties:
Application:
This steel is especially used for ejector pins, tool holders and shrink work chucks. It is majorly widely utilized for manufacture of hot forging die & inserts, hot gripper dies, hot nut tools, hot header dies, brass forging and pressing dies, hot forging aluminum base dies, aluminum casting and extrusion dies, zinc die casting dies, extrusion mandrels, cores, die holder blocks, hot press dies, hot work punches, etc.
Minimum Order Quantity | 200 Kg |
Usage/Application | Construction |
Shape | Round |
Single Piece Length | 3 - 18 Meter |
Technique | Hot Rolled |
Thickness/Diameter | 60 to 1000 mm |
Hardness HB | Max 230 |
Cooling | Furnace |
Soft annealing Degree C | 750 - 800 Deg C |
Hardening Degree C | 1000 - 1030 Deg C |
Process Route
EAF+LF+VD+UPSET+FORGED+ANNEALED+ROUGH TURNED FOR ROUNDS/MILLED FOR FLATS+OIL QUENCHED AND DOUBLE TEMPERED+ROUGH TURNED FOR ROUNDS/MILLED FOR FLATS
Steel Properties :
The exceptional Hot Work Pre-solidified Steel has great toughness and high wear resistance. DB6 Steel is generally provided in hard, quenched, tempered and annealed condition in strengthened condition in exceptional cases. Normally it's working hardness is 360-430 BHN. This steel grade is the updated type of DIN 2713 for higher efficiency and performance.
Application:
Dies for Specially Drop and Close Die Forgings for Hammers & Mechanical Presses, Die Moulds, Shoe Blocks, Die Holder, Piston Rods, Bolster, Cranks, Cassettes, Plastic Moulds, Shearing Blades, Tools etc.
Minimum Order Quantity | 200 Kilogram |
Single Piece Length | 6 meter |
Technique | Hot Rolled |
Application | Construction |
Shape | Rounds |
Hardness HB | max 240 |
Hardening Degree C | 840-900 Deg C |
Hardness after quenching HRC | 55-57 HRC |
Cooling | Furnace |
Soft annealing Degree C | 650-710 Deg C |
Coefficient of thermal expansionat Degree C | 20-700 Deg C |
Diameter | 60 to 1000 mm |
Chemical Composition - (Typical Analysis in %)
STANDARDS | 55NiCrMoV7 | DB6 | DIN 2714 | AISI L6 | AFNOR 55NCDVV7 | JIS SKT4 |
C | Si | Mn | P | S | Cr | Ni | Mo | V |
0.50-0.60 | 0.10-0.40 | 0.65-0.95 | <0.015 | <0.004 | 1.0-1.20 | 1.50-1.80 | 0.45-0.55 | 0.07-0.12 |
USA | Europe | Germany | China | Japan | India | R. of Korea | Russia |
AISI / SAE | En | DIN, WNr | GB | JIS | IS | KS | GOST |
A681 L6 | 55NiCrMoV7 | 56NiCrMoV7 | 5CrNiMo | SKT4 | T55Ni7Cr4Mo5V1 | STF4 | 4ChMNFS |
Ventura Alloy and Steels Stocks and Supplies Die Block Steels DB6 / 2714 in India and abroad. DB6 Steel is an extreme pass on steel with high treating resistance and great through-solidifying properties. Its nickel substance has it uncommonly effect safe – a highly recommendable element for vast mallet & press bites the dust alike. This evaluation is generally supplied in toughened condition or extinguished and tempered to 1300 N/mm² & a working hardness of 370 to 410 HB (round) or 355 to 400 HB (square, level).
Utilized as standard steel for manufacturing passes on of different kinds, press bites the dust, expulsion kicks the bucket, retainer plates, heavily clad trim bites the dust, hot shear sharpened pieces of steels and instrument holder.
Process Route:
EAF+LF+VD+UPSET+FORGED+ANNEALED+ROUGH TURNED FOR ROUNDS/MILLED FOR FLATS+OIL QUENCHED AND DOUBLE TEMPERED+ROUGH TURNED FOR ROUNDS/MILLED FOR FLATS
Steel Properties:
The exceptional Hot Work Pre-solidified Steel has great toughness and high wear resistance. DB6 Steel is generally provided in hard, quenched, tempered and annealed condition in strengthened condition in exceptional cases. Normally it's working hardness is 360-430 BHN. This steel grade is the updated type of DIN 2713 for higher efficiency and performance.
Application:
Dies for Specially Drop and Close Die Forgings for Hammers & Mechanical Presses, Die Moulds, Shoe Blocks, Die Holder, Piston Rods, Bolster, Cranks, Cassettes, Plastic Moulds, Shearing Blades, Tools etc.
Minimum Order Quantity | 200 Kg |
Single Piece Length | 3 - 18 Meter |
Usage/Application | Construction |
Surface Finish | Galvanized |
Shape | Rounds |
Thickness/Diameter | 10 - 500 mm |
Technique | Hot Rolled |
Hardness HB | max 240 |
Hardening Degree C | 1030-1060 Deg C |
Hardness after quenching HRC | 55 HRC |
Cooling | Furnace |
Soft annealing Degree C | 760 - 810 Deg C |
Thermal Conductivity Degree C | 20-700 Deg C |
Chemical Composition - (Typical Analysis in %)
STANDARDS | X40CrMoV5 | H13 | DIN 2344 | AISI H13 | AFNOR Z40CDV5 | JIS SKD61 |
C | Si | Mn | P | S | Cr | Mo | V |
0.35-0.45 | 0.90-1.20 | 0.30-0.50 | <0.03 | <0.004 | 4.90-5.40 | 1.20-1.75 | 0.90-1.20 |
Ventura Alloy and Steels supplies and stocks H13 tool steel in flat, square and round bar. We provide steel in all sizes as your requirements. Consult our team who will assist you for any query related to H13 steel.
SAE AISI H13 steel equivalent with JIS SKD61, GB 4Cr5MoSiV1 and DIN 1.2344 Tool Steel. AISI H13 steel consists of chromium, molybdenum and vanadium and is known for its high hardenability and great toughness.
The molybdenum and vanadium act as strengthening agents while the chromium content helps the AISI H-13 tool steel to withstand softening when used at high temperatures. It also combines shock and abrasion resistance, has good red hardness, can resist rapid cooling and withstand premature heat checking.
H13 Tool Steel has high hot-wear resistance abilities along with great strength, heat conductivity and invulnerability to hot cracking. It has good resistance to abrasion at each low and high temperature. It displays high level of toughness and ductility. H13 has Uniform and high level of machinability and polish ability. It has high-temperature strength and resistance to thermal fatigue, glorious through-hardening properties and shows very limited distortion during hardening.
H3 ESR is the most purified material with the conventional VD route. The nature of material increase the strength, exceptionally increase the micro-cleanness level. H13 ESR is most refined, has greater homogeneity and an exceptionally fine structure, resulting in improved machinability, polishing & high temperature tensile strength. Exceptionally suggest the use of AISI-H13 ESR grade for Aluminum Pressure Die Casting and other part subjected to high working temperatures and high weight quality. H13 is completely ultrasonic examined with 100% positive outcomes according to NDT standards.
Steel Properties:
Great toughness
Thermal conductivity
High hot-wear resistance
Hot tensile strength
Insusceptible for hot cracking (Hot Crack resistant)
Can be water-cooled to a restricted degree
High Hardenability
Application:
This steel is especially used for ejector pins, tool holders and shrink work chucks. It is majorly widely utilized for manufacture of hot forging die & inserts, hot gripper dies, hot nut tools, hot header dies, brass forging and pressing dies, hot forging aluminum base dies, aluminum casting and extrusion dies, zinc die casting dies, extrusion mandrels, cores, die holder blocks, hot press dies, hot work punches, etc.
Minimum Order Quantity | 200 Kg |
Application | Automobile Industry |
Single Piece Length | 3 - 18 Meter |
Shape | Round |
Hardness HB | max 240 |
Hardening Degree C | 1030-1060 Deg C |
Hardness after quenching HRC | 55 HRC |
Cooling | Furnace |
Soft annealing Degree C | 760 - 810 Deg C |
Thermal Conductivity Degree C | 20-700 Deg C |
Diameter | 10 - 500 mm |
Chemical Composition - (Typical Analysis in %)
STANDARDS | X40CrMoV5 | H13 | DIN 2344 | AISI H13 | AFNOR Z40CDV5 | JIS SKD61 |
C | Si | Mn | P | S | Cr | Mo | V |
0.35-0.45 | 0.90-1.20 | 0.30-0.50 | <0.03 | <0.004 | 4.90-5.40 | 1.20-1.75 | 0.90-1.20 |
Ventura Alloy and Steels supplies and stocks H13 tool steel in flat, square and round bar. We provide steel in all sizes as your requirements. Consult our team who will assist you for any query related to H13 steel.
SAE AISI H13 steel equivalent with JIS SKD61, GB 4Cr5MoSiV1 and DIN 1.2344 Tool Steel. AISI H13 steel consists of chromium, molybdenum and vanadium and is known for its high hardenability and great toughness.
The molybdenum and vanadium act as strengthening agents while the chromium content helps the AISI H-13 tool steel to withstand softening when used at high temperatures. It also combines shock and abrasion resistance, has good red hardness, can resist rapid cooling and withstand premature heat checking.
H13 Tool Steel has high hot-wear resistance abilities along with great strength, heat conductivity and invulnerability to hot cracking. It has good resistance to abrasion at each low and high temperature. It displays high level of toughness and ductility. H13 has Uniform and high level of machinability and polish ability. It has high-temperature strength and resistance to thermal fatigue, glorious through-hardening properties and shows very limited distortion during hardening.
H3 ESR is the most purified material with the conventional VD route. The nature of material increase the strength, exceptionally increase the micro-cleanness level. H13 ESR is most refined, has greater homogeneity and an exceptionally fine structure, resulting in improved machinability, polishing & high temperature tensile strength. Exceptionally suggest the use of AISI-H13 ESR grade for Aluminum Pressure Die Casting and other part subjected to high working temperatures and high weight quality. H13 is completely ultrasonic examined with 100% positive outcomes according to NDT standards.
Steel Properties:
Great toughness
Thermal conductivity
High hot-wear resistance
Hot tensile strength
Insusceptible for hot cracking (Hot Crack resistant)
Can be water-cooled to a restricted degree
High Hardenability
Application:
This steel is especially used for ejector pins, tool holders and shrink work chucks. It is majorly widely utilized for manufacture of hot forging die & inserts, hot gripper dies, hot nut tools, hot header dies, brass forging and pressing dies, hot forging aluminum base dies, aluminum casting and extrusion dies, zinc die casting dies, extrusion mandrels, cores, die holder blocks, hot press dies, hot work punches, etc.
Minimum Order Quantity | 200 Kg |
Single Piece Length | 3 - 18 Meter |
Technique | Cold Rolled |
Application | Construction, Automobile Industry |
Hardness HB | Max 250 |
Stress relief annealing Degree C | Approx 660 -710 Deg C |
Hardness after quenching HRC | 63 HRC |
Cooling | Furnace |
Soft annealing Degree C | 840-870 Deg C |
Diameter | 20 to 450 mm |
We are offering X155CRVMO12 Cold Work Stainless Steel Rods to our clients.
Chemical Composition - (Typical Analysis in %)
STANDARDS | X153CrMoV12 | HCHCR-D2 | DIN 2379 | AISI D2 | AFNOR Z160CDV12 | JIS SKD10 |
C | Si | Mn | P | S | Cr | Mo | V |
1.40-1.60 | 0.10-0.60 | 0.20-0.60 | 0.030max | 0.030max | 11.00-13.00 | 0.70-1.00 | 0.80-1.20 |
Ventura Alloy and Steels Supplies and Stocks HCHCR D2 in India and abroad. D2 steel is an air hardening, high-carbon, high-chromium tool steel. It has high wear and abrasion resistant properties. It is heat treatable and will offer a hardness in the range 55-62 HRC, and is machinable in the annealed condition. It tends to be used as threading rolls and dies, icy trimming, cutting & stamping tools for sheet thickness up to 6mm, accuracy cutting instruments for sheet thicknesses up to 12 mm.
Steel Properties:
Application:
HCHCR D2 tool steel can be utilized for cold stamping or forming dies, cold forming rolls, slitters, shear blades, tools, tyre shredders, chipper knives, punches, trimming, cutting threading dies, stamping tools and more.
Physical Properties:
Coefficient of Thermal Expansion at °C | 10-??? m / (m*K) |
20-100 | 10.6 |
20-200 | 11.5 |
20-300 | 11.8 |
20-400 | 12.3 |
Thermal Conductivity at °C | W / (m*K) |
20 | 16.7 |
350 | 20.5 |
700 | 24.2 |
Heat Treatment:
Soft Annealing °C | 840-870 |
Cooling | Furnace |
Hardness HB | max. 250 |
Stress-relief Annealing °C | approx. 660-710 |
Hardening °C | 1000-1050 |
Quenching | Air, Oil, Salt Bath 500-550°C |
Hardness after quenching HRC | 63 |
Tempering°C after quenching | 100 | 200 | 300 | 400 | 500 | 525 | 550 | 600 |
HRC | 64 | 61.5 | 58.5 | 58.5 | 59 | 60 | 57 | 50 |
Minimum Order Quantity | 200 Kilogram |
Single Piece Length | 3 - 18 Meter |
Technique | Hot Rolled |
Application | Automobile Industry |
Shape | Rounds |
Hardness HB | max 240 |
Hardening Degree C | 1030-1060 Deg C |
Soft annealing Degree C | 760 - 810 Deg C |
Cooling | Furnace |
Thermal Conductivity Degree C | 20-700 Deg C |
Diameter | 10 - 500 mm |
Chemical Composition - (Typical Analysis in %)
STANDARDS | X40CrMoV5 | H13 | DIN 2344 | AISI H13 | AFNOR Z40CDV5 | JIS SKD61 |
C | Si | Mn | P | S | Cr | Mo | V |
0.35-0.45 | 0.90-1.20 | 0.30-0.50 | <0.03 | <0.004 | 4.90-5.40 | 1.20-1.75 | 0.90-1.20 |
Ventura Alloy and Steels supplies and stocks H13 tool steel in flat, square and round bar. We provide steel in all sizes as your requirements. Consult our team who will assist you for any query related to H13 steel.
SAE AISI H13 steel equivalent with JIS SKD61, GB 4Cr5MoSiV1 and DIN 1.2344 Tool Steel. AISI H13 steel consists of chromium, molybdenum and vanadium and is known for its high hardenability and great toughness.
The molybdenum and vanadium act as strengthening agents while the chromium content helps the AISI H-13 tool steel to withstand softening when used at high temperatures. It also combines shock and abrasion resistance, has good red hardness, can resist rapid cooling and withstand premature heat checking.
H13 Tool Steel has high hot-wear resistance abilities along with great strength, heat conductivity and invulnerability to hot cracking. It has good resistance to abrasion at each low and high temperature. It displays high level of toughness and ductility. H13 has Uniform and high level of machinability and polish ability. It has high-temperature strength and resistance to thermal fatigue, glorious through-hardening properties and shows very limited distortion during hardening.
H3 ESR is the most purified material with the conventional VD route. The nature of material increase the strength, exceptionally increase the micro-cleanness level. H13 ESR is most refined, has greater homogeneity and an exceptionally fine structure, resulting in improved machinability, polishing & high temperature tensile strength. Exceptionally suggest the use of AISI-H13 ESR grade for Aluminum Pressure Die Casting and other part subjected to high working temperatures and high weight quality. H13 is completely ultrasonic examined with 100% positive outcomes according to NDT standards.
Steel Properties
Great toughness
Thermal conductivity
High hot-wear resistance
Hot tensile strength
Insusceptible for hot cracking (Hot Crack resistant)
Can be water-cooled to a restricted degree
High Hardenability
Application:
This steel is especially used for ejector pins, tool holders and shrink work chucks. It is majorly widely utilized for manufacture of hot forging die & inserts, hot gripper dies, hot nut tools, hot header dies, brass forging and pressing dies, hot forging aluminum base dies, aluminum casting and extrusion dies, zinc die casting dies, extrusion mandrels, cores, die holder blocks, hot press dies, hot work punches, etc.
Minimum Order Quantity | 200 Kilogram |
Single Piece Length | 3 - 18 Meter |
Usage/Application | Construction |
Surface Finish | Galvanized |
Shape | Round |
Diameter | 71 - 300 mm |
Hardness HB | max 230 |
Hardening Degree C | 1000-1030 Deg C |
Hardness after quenching HRC | 54 HRC |
Cooling | Furnace |
Chemical Composition - (Typical Analysis in %)
STANDARDS | X37CrMoV5 | H11 | DIN 2343 | AISI H11 | AFNOR Z38CDV5 | JIS SKD6 |
C | Si | Mn | P | S | Cr | Mo | V |
0.33-0.41 | 0.80-1.00 | 0.25-0.50 | 0.003 max | 0.030max | 4.80-5.50 | 1.10-1.50 | 0.30-0.50 |
USA | Europe | Germany | China | Japan | India | R. of Korea | Russia |
AISI / SAE | En | DIN, WNr | GB | JIS | IS | KS | GOST |
H11 | X37CrMoV5-1 | X38CrMoV5-1 | 4Cr5MoSiV | SKD6 | XT35Cr5Mo1V3 | STD 6 | 4Ch5MFS |
Ventura Alloy and Steels Supplies and Stocks AISI H11 tool steel is a 5% chromium hot work tool steel that is represented by its excellent impact toughness. Chromium hot-work tool steels are designated as group H steels according to the AISI classification system, and specified in ASTM A681 standard. The most commonly used chromium hot-work steels are H11 tool steel, H12 tool steel, and H13 steel, within the series from H1 to H19.
If we compare between H11 and H13, H11 tool steel consists of less vanadium than the commonly used H13 hot work tool steel. This gives H11 steels the higher toughness, with some reduction in wear resistance and tamper resistance. H11 tool steel is a deep-hardening, air-hardening steel and H11 alloy steel could be deep hardened by heat treatment and air-quenching. That gives minimal size change during heat treatment. H11 how work steel also has super resistance to thermal fatigue cracking and superb resistance to gross cracking and thermal shock when water cooled in service.
H11 steel is inclusive of all hot work tool steel with excellent rigidity and durability along with great thermal conductivity and invulnerability to hot cracking and can be water cooled to a constrained degree. H11 is primarily used for apparatus holders , ejector pins and shrink fit chucks.
STEEL PROPERTIES
Contains 5% Chromium
Greater strength
High toughness
Best thermal physical phenomenon
Resistant to hot cracking
Gives fundamental necessities to long tool life in press forging, die-casting, extrusion processes etc.
APPLICATION
This grade isn't utilized for typical applications in the area of hot-work steels, yet additionally useful for tool holders, bridge kind tools, ejector pins, liner holders, hot work punches, forging dies, and shrink work chucks.
SIZE RANGE
ROUNDS - 71 to 300 MM DIA
FLATS - Thickness - 20 to 400 MM MAX | Width - 40 to 700 MM MAX
PRICE RANGE - Rs.130-180 per Kg
STOCKING PARTNERS
We keep the materials from China.
Minimum Order Quantity | 200 Kilogram |
Usage/Application | Construction |
Single Piece Length | 3 - 18 Meter |
Technique | Hot Rolled |
Shape | Rounds |
Thickness/Diameter | 60 - 1000 mm |
Hardness HB | Max 240 |
Hardening Degree C | 840-900 Deg C |
Hardness after quenching HRC | 55-57 HRC |
Cooling | Furnace |
We are manufacturer and supplier Of 2714 Steel Round Bars.
Chemical Composition - (Typical Analysis in %)
STANDARDS | 55NiCrMoV7 | DB6 | DIN 2714 | AISI L6 | AFNOR 55NCDVV7 | JIS SKT4 |
C | Si | Mn | P | S | Cr | Ni | Mo | V |
0.50-0.60 | 0.10-0.40 | 0.65-0.95 | <0.015 | <0.004 | 1.0-1.20 | 1.50-1.80 | 0.45-0.55 | 0.07-0.12 |
USA | Europe | Germany | China | Japan | India | R. of Korea | Russia |
AISI / SAE | En | DIN, WNr | GB | JIS | IS | KS | GOST |
A681 L6 | 55NiCrMoV7 | 56NiCrMoV7 | 5CrNiMo | SKT4 | T55Ni7Cr4Mo5V1 | STF4 | 4ChMNFS |
Ventura Alloy and Steels Stocks and Supplies Die Block Steels DB6 / 2714 in India and abroad. DB6 Steel is an extreme pass on steel with high treating resistance and great through-solidifying properties. Its nickel substance has it uncommonly effect safe – a highly recommendable element for vast mallet & press bites the dust alike. This evaluation is generally supplied in toughened condition or extinguished and tempered to 1300 N/mm² & a working hardness of 370 to 410 HB (round) or 355 to 400 HB (square, level).
Utilized as standard steel for manufacturing passes on of different kinds, press bites the dust, expulsion kicks the bucket, retainer plates, heavily clad trim bites the dust, hot shear sharpened pieces of steels and instrument holder.
Utilized as standard steel for manufacturing passes on of different kinds, press bites the dust, expulsion kicks the bucket, retainer plates, heavily clad trim bites the dust, hot shear sharpened pieces of steels and instrument holder.
Process Route:
Eaf+Lf+Vd+Upset+Forged+Annealed+Rough Turned For Rounds/Milled For Flats+Oil Quenched And Double Tempered+ Rough Turned For Rounds/Milled For Flats
Steel Properties:
The special Hot Work Pre-hardened Steel has great toughness and high wear resistance. DB6 Steel is generally supplied in hard, quenched, tempered and also in annealed condition in special cases. Usually it's working hardness is 360-430 BHN. This steel grade is the upgraded version of DIN 2713 for greater efficiency and performance.
Application:
Dies for Specially Drop and Close Die Forgings for Hammers & Mechanical Presses, Die Moulds, Shoe Blocks, Die Holder, Cassettes, Piston Rods, Cranks, Boaster, Shearing Blades, Tools, Plastic Moulds etc.
Minimum Order Quantity | 200 Kg |
Material Grade | EN24 |
Single Piece Length | 3 - 18 Meter |
Usage/Application | Construction |
Shape | Round |
Surface Finish | Polished |
Material | Alloy Steel |
Thickness/Diameter | 6 - 450 mm Dia. |
Standard | Grade | C | Mn | P | S | Si | Ni | Cr | Mo |
ASTM A29 | 4340 | 0.38-0.43 | 0.60-0.80 | 0.035 max | 0.040 max | 0.15-0.35 | 1.65-2.00 | 0.70-0.90 | 0.20-0.30 |
EN 10250 | 36CrNiMo4 / 1.6511 | 0.32-0.40 | 0.50-0.80 | 0.035 max | 0.035 max | 0.40 max | 0.90-1.20 | 0.90-1.2 | 0.15-0.30 |
BS 970 | EN24 / 817M40 | 0.36-0.44 | 0.45-0.70 | 0.035 max | 0.040 max | 0.10-0.40 | 1.30-1.70 | 1.00-1.40 | 0.20-0.35 |
JIS G4103 | SNCM 439 / SNCM 8 | 0.36-0.43 | 0.60-0.90 | 0.035 max | 0.030 max | 0.15-0.35 | 1.60-2.00 | 0.60-1.00 | 0.15-0.30 |
Thermal Conductivity at °C | W / (m*K) |
20 | 40.5 |
350 | 32.5 |
700 | 25.5 |
Soft Annealing °C | 650-700 |
Cooling | Slowly |
Hardness HB | max. 280 |
Stress-relief Annealing °C | 630-650 |
Cooling | Furnace |
1st Pre-Heating °C | up to approx. 400 in an air-circulating furnace |
2nd and 3rd | 780 and 1000 |
Hardening °C | 1190-1230 |
Quenching | Salt Bath, at least 520°C Oil, Air |
Tempering °C | at least twice 530-560 |
Hardness after Temperature HRC | 64-66 |
Minimum Order Quantity | 200 Kilogram |
Usage/Application | Construction |
Shape | Round |
Single Piece Length | 6 meter |
Technique | Cold Rolled |
Thickness/Diameter | 20 to 450 mm |
Stress relief annealing C | Approx 660-710 |
Cooling | Furnace |
Hardening Degree C | 1000-1050 Deg C |
Quenching | Air, Oil or Salt Bath, 500-550 Degree C |
Hardness after quenching HRC | 63 HRC |
Chemical Composition - (Typical Analysis in %)
STANDARDS | X153CrMoV12 | HCHCR-D2 | DIN 2379 | AISI D2 | AFNOR Z160CDV12 | JIS SKD10 |
C | Si | Mn | P | S | Cr | Mo | V |
1.40-1.60 | 0.10-0.60 | 0.20-0.60 | 0.030max | 0.030max | 11.00-13.00 | 0.70-1.00 | 0.80-1.20 |
Ventura Alloy and Steels Supplies and Stocks HCHCR D2 in India and abroad. D2 steel is an air hardening, high-carbon, high-chromium tool steel. It has high wear and abrasion resistant properties. It is heat treatable and will offer a hardness in the range 55-62 HRC, and is machinable in the annealed condition. It tends to be used as threading rolls and dies, icy trimming, cutting & stamping tools for sheet thickness up to 6mm, accuracy cutting instruments for sheet thicknesses up to 12 mm.
Steel Properties:
Application:
HCHCR D2 tool steel can be utilized for cold stamping or forming dies, cold forming rolls, slitters, shear blades, tools, tyre shredders, chipper knives, punches, trimming, cutting threading dies, stamping tools and more.
Physical Properties:
Coefficient of Thermal Expansion at °C | 10-??? m / (m*K) |
20-100 | 10.6 |
20-200 | 11.5 |
20-300 | 11.8 |
20-400 | 12.3 |
Thermal Conductivity at °C | W / (m*K) |
20 | 16.7 |
350 | 20.5 |
700 | 24.2 |
Heat Treatment:
Soft Annealing °C | 840-870 |
Cooling | Furnace |
Hardness HB | max. 250 |
Stress-relief Annealing °C | approx. 660-710 |
Hardening °C | 1000-1050 |
Quenching | Air, Oil, Salt Bath 500-550°C |
Hardness after quenching HRC | 63 |
Tempering°C after quenching | 100 | 200 | 300 | 400 | 500 | 525 | 550 | 600 |
HRC | 64 | 61.5 | 58.5 | 58.5 | 59 | 60 | 57 | 50 |
Price Range:
Material Grade | As per your requirement |
Single Piece Length | All length Available |
Brand | Ventura Alloy And Steel Private Limited |
Usage/Application | All uses |
Shape | All Shapes Available |
Size | As Per Your Requirement |
Surface Finish | All finish Available |
Material | As per your requirement |
Thickness/Diameter | All Available |
Delivery Details | 3-5 days |
Minimum Order Quantity | 200 Kg |
Application | Construction |
Single Piece Length | 3 - 18 Meter |
Surface Finish | Polished |
Material | Alloy Steel |
Thickness/Diameter | 6 - 450 mm Dia. |
Shape | Round |
Standard | Grade | C | Mn | P | S | Si | Ni | Cr | Mo |
ASTM A29 | 4340 | 0.38-0.43 | 0.60-0.80 | 0.035 max | 0.040 max | 0.15-0.35 | 1.65-2.00 | 0.70-0.90 | 0.20-0.30 |
EN 10250 | 36CrNiMo4 / 1.6511 | 0.32-0.40 | 0.50-0.80 | 0.035 max | 0.035 max | 0.40 max | 0.90-1.20 | 0.90-1.2 | 0.15-0.30 |
BS 970 | EN24 / 817M40 | 0.36-0.44 | 0.45-0.70 | 0.035 max | 0.040 max | 0.10-0.40 | 1.30-1.70 | 1.00-1.40 | 0.20-0.35 |
JIS G4103 | SNCM 439 / SNCM 8 | 0.36-0.43 | 0.60-0.90 | 0.035 max | 0.030 max | 0.15-0.35 | 1.60-2.00 | 0.60-1.00 | 0.15-0.30 |
Thermal Conductivity at °C | W / (m*K) |
20 | 40.5 |
350 | 32.5 |
700 | 25.5 |
Soft Annealing °C | 650-700 |
Cooling | Slowly |
Hardness HB | max. 280 |
Stress-relief Annealing °C | 630-650 |
Cooling | Furnace |
1st Pre-Heating °C | up to approx. 400 in an air-circulating furnace |
2nd and 3rd | 780 and 1000 |
Hardening °C | 1190-1230 |
Quenching | Salt Bath, at least 520°C Oil, Air |
Tempering °C | at least twice 530-560 |
Hardness after Temperature HRC | 64-66 |
Minimum Order Quantity | 200 Onwards |
Usage/Application | Construction |
Single Piece Length | 3 - 18 Meter |
Technique | Hot Rolled |
Shape | Round |
Thickness/Diameter | 10 to 500 mm |
Soft annealing Degree C | 760 - 810 Deg C |
Tempering Degree C | 100-700 Deg C |
Hardness after quenching HRC | 55 HRC |
Hardness HB | Max 240 |
Cooling | Furnace |
Thermal Conductivity Degree C | 20-700 Deg C |
We are offering H13 Hot Die Stainless Steel Rods to our clients.
Chemical Composition - (Typical Analysis in %)
STANDARDS | X40CrMoV5 | H13 | DIN 2344 | AISI H13 | AFNOR Z40CDV5 | JIS SKD61 |
C | Si | Mn | P | S | Cr | Mo | V |
0.35-0.45 | 0.90-1.20 | 0.30-0.50 | <0.03 | <0.004 | 4.90-5.40 | 1.20-1.75 | 0.90-1.20 |
Ventura Alloy and Steels supplies and stocks H13 tool steel in flat, square and round bar. We provide steel in all sizes as your requirements. Consult our team who will assist you for any query related to H13 steel.
SAE AISI H13 steel equivalent with JIS SKD61, GB 4Cr5MoSiV1 and DIN 1.2344 Tool Steel. AISI H13 steel consists of chromium, molybdenum and vanadium and is known for its high hardenability and great toughness.
The molybdenum and vanadium act as strengthening agents while the chromium content helps the AISI H-13 tool steel to withstand softening when used at high temperatures. It also combines shock and abrasion resistance, has good red hardness, can resist rapid cooling and withstand premature heat checking.
H13 Tool Steel has high hot-wear resistance abilities along with great strength, heat conductivity and invulnerability to hot cracking. It has good resistance to abrasion at each low and high temperature. It displays high level of toughness and ductility. H13 has Uniform and high level of machinability and polish ability. It has high-temperature strength and resistance to thermal fatigue, glorious through-hardening properties and shows very limited distortion during hardening.
H3 ESR is the most purified material with the conventional VD route. The nature of material increase the strength, exceptionally increase the micro-cleanness level. H13 ESR is most refined, has greater homogeneity and an exceptionally fine structure, resulting in improved machinability, polishing & high temperature tensile strength. Exceptionally suggest the use of AISI-H13 ESR grade for Aluminum Pressure Die Casting and other part subjected to high working temperatures and high weight quality. H13 is completely ultrasonic examined with 100% positive outcomes according to NDT standards.
Steel Properties:
Great toughness
Thermal conductivity
High hot-wear resistance
Hot tensile strength
Insusceptible for hot cracking (Hot Crack resistant)
Can be water-cooled to a restricted degree
High Hardenability
Application:
This steel is especially used for ejector pins, tool holders and shrink work chucks. It is majorly widely utilized for manufacture of hot forging die & inserts, hot gripper dies, hot nut tools, hot header dies, brass forging and pressing dies, hot forging aluminum base dies, aluminum casting and extrusion dies, zinc die casting dies, extrusion mandrels, cores, die holder blocks, hot press dies, hot work punches, etc.
Minimum Order Quantity | 1000 Onwards |
Single Piece Length | 3 - 18 Meter |
Technique | Cold Rolled |
Application | Construction, Automobile Industry |
Hardening Degree C | 78 - 820 Deg C |
Hardness HB | Max 230 |
Thermal Conductivity at Degree C | 20-700 Deg C |
Cooling | Furnace |
Finishing | Polished |
Diameter | 60 - 500 mm |
Minimum Order Quantity | 200 Kg |
Shape | Round |
Application | Automobile Industry, Pharmaceutical / Chemical Industry, Construction |
Material | spring Steel |
Hardness Tolerance | 3 HRC |
Hardness HB | Max 240 |
Cooling | Furnace |
Hardening Degree C | 840-900 Deg C |
Hardness after quenching HRC | 55-57 HRC |
Forging Ratio | 41 |
Diameter | 60 to 1000 mm |
Ventura Alloy and Steels Stocks and Supplies Stainless Steel Round Bars in India and abroad. DB6 Steel is an extreme pass on steel with high treating resistance and great through-solidifying properties. Its nickel substance has it uncommonly effect safe – a highly recommendable element for vast mallet & press bites the dust alike. This evaluation is generally supplied in toughened condition or extinguished and tempered to 1300 N/mm² & a working hardness of 370 to 410 HB (round) or 355 to 400 HB (square, level).
Utilized as standard steel for manufacturing passes on of different kinds, press bites the dust, expulsion kicks the bucket, retainer plates, heavily clad trim bites the dust, hot shear sharpened pieces of steels and instrument holder.
Utilized as standard steel for manufacturing passes on of different kinds, press bites the dust, expulsion kicks the bucket, retainer plates, heavily clad trim bites the dust, hot shear sharpened pieces of steels and instrument holder.
Process Route:
Eaf+Lf+Vd+Upset+Forged+Annealed+Rough Turned For Rounds/Milled For Flats+Oil Quenched And Double Tempered+ Rough Turned For Rounds/Milled For Flats
Steel Properties:
The special Hot Work Pre-hardened Steel has great toughness and high wear resistance. DB6 Steel is generally supplied in hard, quenched, tempered and also in annealed condition in special cases. Usually it's working hardness is 360-430 BHN. This steel grade is the upgraded version of DIN 2713 for greater efficiency and performance.
Application:
Dies for Specially Drop and Close Die Forgings for Hammers & Mechanical Presses, Die Moulds, Shoe Blocks, Die Holder, Cassettes, Piston Rods, Cranks, Boaster, Shearing Blades, Tools, Plastic Moulds etc.
Minimum Order Quantity | 200 Kilogram |
Single Piece Length | 3 - 18 Meter |
Shape | Round |
Hardness HB | max 240 |
Hardening Degree C | 1030-1130 |
Hardness after quenching HRC | 57 |
Cooling | Furnace |
Soft annealing Degree C | 820 |
Coefficient of thermal expansionat Degree C | 20-500 |
Quenching | Oil or Hot Bath 500-550 Degree C |
Material | Alloy Steel |
Chemical Composition - (Typical Analysis in %)
STANDARDS |
X37CrMoW5-1 |
H12 |
DIN 2606 |
AISI H12 |
AFNOR 32CDV12-28 |
JIS SKD62 |
C |
Si |
Mn |
P |
S |
Cr |
W |
Mo |
V |
0.30-0.40 |
0.80-1.25 |
0.20-0.60 |
0.003 max |
0.030max |
4.75-5.50 |
1.00-1.70 |
1.25-1.75 |
0.20-0.50 |
USA |
Germany |
Japan |
British |
AISI / SAE |
DIN, WNr |
JIS G4404 |
BS 4659 |
H12 / T20812 |
1.2605 / X35CrWMoV5 |
SKD62 |
BH12 |
H12 Hot Work Die Steel could be a five-hitter Cr, general hot work steel that is characterized by wonderful effect strength. It contains less vanadium than the broadly utilized H13 hot work tool steel, and furthermore the tungsten content gives higher temper resistance. It has smart resistance to thermal fatigue cracking (heat checking) and excellent resistance to gross cracking and thermal shock once water cooled in commission. TLS H12 hot work tool steel is normally prescribed for warm tooling applications wherever most resistance from cracking is required. Such applications grasp die casting, hot punches, hot shear cutting edges, shaping dies, extrusion tooling and hot gripper dies.
Steel Properties:
Physical Properties:
Coefficient of Thermal Expansion at °C |
10¯??? m / (m*K) |
20-100 |
11.7 |
20-250 |
12.4 |
20-500 |
12.9 |
Price Range: Rs.350 to 750/ Kg
Minimum Order Quantity | 1000 Kg |
Usage/Application | Construction |
Shape | Round |
Single Piece Length | 3 - 18 Meter |
Technique | Cold Rolled |
Thickness/Diameter | 60 to 1000 mm |
Hardening Degree C | 780 - 820 Deg C |
Cooling | Furnace |
Thermal Conductivity at Degree C | 20 - 700 Deg C |
Tempering Degree C after Quenching | 100 - 600 Deg C |
Finishing | Polished |
Minimum Order Quantity | 200 Kg |
Usage/Application | Construction |
Single Piece Length | 18 meter |
Technique | Hot Rolled |
Shape | Rounds |
Thickness/Diameter | 60 - 1000 mm |
Soft annealing Degree C | 650-710 |
Quenching | Oil,Air |
Hardness after quenching HRC | 55-57 |
Hardness HB | Max. 240 |
Cooling | Furnace |
Hardening Degree C | 840-900 |
Thermal Conductivity Degree C | 20-700 |
We are offering Hot Work Steel Round Rods to our clients.
Chemical Composition - (Typical Analysis in %)
STANDARDS | 55NiCrMoV7 | DB6 | DIN 2714 | AISI L6 | AFNOR 55NCDVV7 | JIS SKT4 |
C | Si | Mn | P | S | Cr | Ni | Mo | V |
0.50-0.60 | 0.10-0.40 | 0.65-0.95 | <0.015 | <0.004 | 1.0-1.20 | 1.50-1.80 | 0.45-0.55 | 0.07-0.12 |
USA | Europe | Germany | China | Japan | India | R. of Korea | Russia |
AISI / SAE | En | DIN, WNr | GB | JIS | IS | KS | GOST |
A681 L6 | 55NiCrMoV7 | 56NiCrMoV7 | 5CrNiMo | SKT4 | T55Ni7Cr4Mo5V1 | STF4 | 4ChMNFS |
Ventura Alloy and Steels Stocks and Supplies Die Block Steels DB6 / 2714 in India and abroad. DB6 Steel is an extreme pass on steel with high treating resistance and great through-solidifying properties. Its nickel substance has it uncommonly effect safe – a highly recommendable element for vast mallet & press bites the dust alike. This evaluation is generally supplied in toughened condition or extinguished and tempered to 1300 N/mm² & a working hardness of 370 to 410 HB (round) or 355 to 400 HB (square, level).
Utilized as standard steel for manufacturing passes on of different kinds, press bites the dust, expulsion kicks the bucket, retainer plates, heavily clad trim bites the dust, hot shear sharpened pieces of steels and instrument holder.
Process Route:
Eaf+Lf+Vd+Upset+Forged+Annealed+Rough Turned For Rounds/Milled For Flats+Oil Quenched And Double Tempered+ Rough Turned For Rounds/Milled For Flats
Steel Properties:
The special Hot Work Pre-hardened Steel has great toughness and high wear resistance. DB6 Steel is generally supplied in hard, quenched, tempered and also in annealed condition in special cases. Usually it's working hardness is 360-430 BHN. This steel grade is the upgraded version of DIN 2713 for greater efficiency and performance.
Application:
Dies for Specially Drop and Close Die Forgings for Hammers & Mechanical Presses, Die Moulds, Shoe Blocks, Die Holder, Cassettes, Piston Rods, Cranks, Boaster, Shearing Blades, Tools, Plastic Moulds etc.
Minimum Order Quantity | 200 Kg |
Usage/Application | Construction |
Single Piece Length | 3 - 18 Meter |
Technique | Hot Rolled |
Shape | Rounds |
Thickness/Diameter | 10 - 500 mm |
Hardness HB | Max 240 |
Hardening Degree C | 1030-1060 Deg C |
Hardness after quenching HRC | 55 HRC |
Cooling | Furnace |
Soft annealing Degree C | 760 - 810 Deg C |
Thermal Conductivity Degree C | 20-700 Deg C |
We are offering X40CRMOV5-1 Stainless Stel Rodsto our clients.
Chemical Composition - (Typical Analysis in %)
STANDARDS | X40CrMoV5 | H13 | DIN 2344 | AISI H13 | AFNOR Z40CDV5 | JIS SKD61 |
C | Si | Mn | P | S | Cr | Mo | V |
0.35-0.45 | 0.90-1.20 | 0.30-0.50 | <0.03 | <0.004 | 4.90-5.40 | 1.20-1.75 | 0.90-1.20 |
Ventura Alloy and Steels supplies and stocks H13 tool steel in flat, square and round bar. We provide steel in all sizes as your requirements. Consult our team who will assist you for any query related to H13 steel.
SAE AISI H13 steel equivalent with JIS SKD61, GB 4Cr5MoSiV1 and DIN 1.2344 Tool Steel. AISI H13 steel consists of chromium, molybdenum and vanadium and is known for its high hardenability and great toughness.
The molybdenum and vanadium act as strengthening agents while the chromium content helps the AISI H-13 tool steel to withstand softening when used at high temperatures. It also combines shock and abrasion resistance, has good red hardness, can resist rapid cooling and withstand premature heat checking.
H13 Tool Steel has high hot-wear resistance abilities along with great strength, heat conductivity and invulnerability to hot cracking. It has good resistance to abrasion at each low and high temperature. It has high-temperature strength and resistance to thermal fatigue, glorious through-hardening properties and shows very limited distortion during hardening.
H3 ESR is the most purified material with the conventional VD route. The nature of material increase the strength, exceptionally increase the micro-cleanness level. Exceptionally suggest the use of AISI-H13 ESR grade for Aluminum Pressure Die Casting and other part subjected to high working temperatures and high weight quality. H13 is completely ultrasonic examined with 100% positive outcomes according to NDT standards.
Steel Properties:
· Great toughness
· Thermal conductivity
· High hot-wear resistance
· Hot tensile strength
· Insusceptible for hot cracking (Hot Crack resistant)
· Can be water-cooled to a restricted degree
· High Hardenability
Application:
This steel is especially used for ejector pins, tool holders and shrink work chucks. It is majorly widely utilized for manufacture of hot forging die & inserts, hot gripper dies, hot nut tools, hot header dies, brass forging and pressing dies, hot forging aluminum base dies, aluminum casting and extrusion dies, zinc die casting dies, extrusion mandrels, cores, die holder blocks, hot press dies, hot work punches, etc.
Size Range:
ROUNDS - 10 to 500 MM DIA
FLATS - Thickness - 20 to 400 MM MAX | Width - 40 to 700 MM MAX
Price Range:
Rs.150 to 230 per Kg
Stocking Partners:
We keep the materials from Germany and China.
Minimum Order Quantity | 200 Kg |
Usage/Application | Construction |
Single Piece Length | 3 - 18 Meter |
Technique | Hot Rolled |
Shape | Rounds |
Thickness/Diameter | 60 to 1000 mm |
Soft annealing Degree C | 650-710 Deg C |
Cooling | Furnace |
Hardness HB | Max 240 |
Hardening Degree C | 840 - 900 Deg C |
Hardness after quenching HRC | 55 - 57 HRC |
Coefficient of thermal expansionat Degree C | 20-700 Deg C |
Chemical Composition - (Typical Analysis in %)
STANDARDS | 55NiCrMoV7 | DB6 | DIN 2714 | AISI L6 | AFNOR 55NCDVV7 | JIS SKT4 |
C | Si | Mn | P | S | Cr | Ni | Mo | V |
0.50-0.60 | 0.10-0.40 | 0.65-0.95 | <0.015 | <0.004 | 1.0-1.20 | 1.50-1.80 | 0.45-0.55 | 0.07-0.12 |
USA | Europe | Germany | China | Japan | India | R. of Korea | Russia |
AISI / SAE | En | DIN, WNr | GB | JIS | IS | KS | GOST |
A681 L6 | 55NiCrMoV7 | 56NiCrMoV7 | 5CrNiMo | SKT4 | T55Ni7Cr4Mo5V1 | STF4 | 4ChMNFS |
Ventura Alloy and Steels Stocks and Supplies Die Block Steels DB6 / 2714 in India and abroad. DB6 Steel is an extreme pass on steel with high treating resistance and great through-solidifying properties. Its nickel substance has it uncommonly effect safe – a highly recommendable element for vast mallet & press bites the dust alike. This evaluation is generally supplied in toughened condition or extinguished and tempered to 1300 N/mm² & a working hardness of 370 to 410 HB (round) or 355 to 400 HB (square, level).
Utilized as standard steel for manufacturing passes on of different kinds, press bites the dust, expulsion kicks the bucket, retainer plates, heavily clad trim bites the dust, hot shear sharpened pieces of steels and instrument holder.
Process Route
EAF+LF+VD+UPSET+FORGED+ANNEALED+ROUGH TURNED FOR ROUNDS/MILLED FOR FLATS+OIL QUENCHED AND DOUBLE TEMPERED+ROUGH TURNED FOR ROUNDS/MILLED FOR FLATS
Steel Properties:
The exceptional Hot Work Pre-solidified Steel has great toughness and high wear resistance. DB6 Steel is generally provided in hard, quenched, tempered and annealed condition in strengthened condition in exceptional cases. Normally it's working hardness is 360-430 BHN. This steel grade is the updated type of DIN 2713 for higher efficiency and performance.
Application:
Dies for Specially Drop and Close Die Forgings for Hammers & Mechanical Presses, Die Moulds, Shoe Blocks, Die Holder, Piston Rods, Bolster, Cranks, Cassettes, Plastic Moulds, Shearing Blades, Tools etc.
Minimum Order Quantity | 200 Kg |
Single Piece Length | 3 - 18 Meter |
Usage/Application | Construction |
Surface Finish | Galvanized |
Shape | Rounds |
Thickness/Diameter | 60 - 1000 mm |
Technique | Hot Rolled |
Hardening Degree C | 840 - 900 Deg C |
Hardness after quenching HRC | 55 - 57 HRC |
Hardness HB | Max 240 |
Cooling | Furnace |
We are manufacturer and supplier Of DB6 Hot Die Steel Rods.
Chemical Composition - (Typical Analysis in %)
STANDARDS | 55NiCrMoV7 | DB6 | DIN 2714 | AISI L6 | AFNOR 55NCDVV7 | JIS SKT4 |
C | Si | Mn | P | S | Cr | Ni | Mo | V |
0.50-0.60 | 0.10-0.40 | 0.65-0.95 | <0.015 | <0.004 | 1.0-1.20 | 1.50-1.80 | 0.45-0.55 | 0.07-0.12 |
USA | Europe | Germany | China | Japan | India | R. of Korea | Russia |
AISI / SAE | En | DIN, WNr | GB | JIS | IS | KS | GOST |
A681 L6 | 55NiCrMoV7 | 56NiCrMoV7 | 5CrNiMo | SKT4 | T55Ni7Cr4Mo5V1 | STF4 | 4ChMNFS |
Ventura Alloy and Steels Stocks and Supplies Die Block Steels DB6 / 2714 in India and abroad. DB6 Steel is an extreme pass on steel with high treating resistance and great through-solidifying properties. Its nickel substance has it uncommonly effect safe – a highly recommendable element for vast mallet & press bites the dust alike. This evaluation is generally supplied in toughened condition or extinguished and tempered to 1300 N/mm² & a working hardness of 370 to 410 HB (round) or 355 to 400 HB (square, level).
Utilized as standard steel for manufacturing passes on of different kinds, press bites the dust, expulsion kicks the bucket, retainer plates, heavily clad trim bites the dust, hot shear sharpened pieces of steels and instrument holder.
Utilized as standard steel for manufacturing passes on of different kinds, press bites the dust, expulsion kicks the bucket, retainer plates, heavily clad trim bites the dust, hot shear sharpened pieces of steels and instrument holder.
Process Route:
Eaf+Lf+Vd+Upset+Forged+Annealed+Rough Turned For Rounds/Milled For Flats+Oil Quenched And Double Tempered+ Rough Turned For Rounds/Milled For Flats
Steel Properties:
The special Hot Work Pre-hardened Steel has great toughness and high wear resistance. DB6 Steel is generally supplied in hard, quenched, tempered and also in annealed condition in special cases. Usually it's working hardness is 360-430 BHN. This steel grade is the upgraded version of DIN 2713 for greater efficiency and performance.
Application:
Dies for Specially Drop and Close Die Forgings for Hammers & Mechanical Presses, Die Moulds, Shoe Blocks, Die Holder, Cassettes, Piston Rods, Cranks, Boaster, Shearing Blades, Tools, Plastic Moulds etc.
Minimum Order Quantity | 200 Kg |
Application | Automobile Industry |
Single Piece Length | 3 - 18 Meter |
Technique | Hot Rolled |
Shape | Round |
Diameter | 71 - 300 mm |
Material | Spring Steel |
Hardness HB | Max 230 |
Hardening Degree C | 1000-1030 Deg C |
Hardness after quenching HRC | 54 HRC |
Cooling | Furnace |
We are offering 2343 Die Steel Round Bars to our clients.
Chemical Composition - (Typical Analysis in %)
STANDARDS | X37CrMoV5 | H11 | DIN 2343 | AISI H11 | AFNOR Z38CDV5 | JIS SKD6 |
C | Si | Mn | P | S | Cr | Mo | V |
0.33-0.41 | 0.80-1.00 | 0.25-0.50 | 0.003 max | 0.030max | 4.80-5.50 | 1.10-1.50 | 0.30-0.50 |
USA | Europe | Germany | China | Japan | India | R. of Korea | Russia |
AISI / SAE | En | DIN, WNr | GB | JIS | IS | KS | GOST |
H11 | X37CrMoV5-1 | X38CrMoV5-1 | 4Cr5MoSiV | SKD6 | XT35Cr5Mo1V3 | STD 6 | 4Ch5MFS |
Ventura Alloy and Steels Supplies and Stocks AISI H11 tool steel is a 5% chromium hot work tool steel that is represented by its excellent impact toughness. The most commonly used chromium hot-work steels are H11 tool steel, and H13 steel, within the series from H1 to H19.
If we compare between H11 and H13, H11 tool steel consists of less vanadium than the commonly used H13 hot work tool steel. This gives H11 steels the higher toughness, with some reduction in wear resistance and tamper resistance. H11 tool steel is a deep-hardening, air-hardening steel and H11 alloy steel could be deep hardened by heat treatment and air-quenching. That gives minimal size change during heat treatment. H11 how work steel also has super resistance to thermal fatigue cracking and superb resistance to gross cracking and thermal shock when water cooled in service.
H11 steel is inclusive of all hot work tool steel with excellent rigidity and durability along with great thermal conductivity and invulnerability to hot cracking and can be water cooled to a constrained degree. H11 is primarily used for apparatus holders ,ejector pins and shrink fit chucks.
Steel Properties:
Application:
This grade isn't utilized for typical applications in the area of hot-work steels, yet additionally useful for tool holders, bridge kind tools, ejector pins, liner holders, hot work punches, forging dies, and shrink work chucks.
Minimum Order Quantity | 200 Kilogram |
Usage/Application | Construction |
Shape | Round |
Single Piece Length | 3 - 18 Meter |
Technique | Cold Rolled |
Thickness/Diameter | 50 - 500 mm |
Material | Alloy Steel |
Coefficient of thermal expansionat Degree C | 20-400 Deg C |
Thermal Conductivity at Degree C | 20-700 Deg C |
Soft annealing Degree C | 840-870 Deg C |
Cooling | Furnace |
Hardness HB | Max. 250 |
Hardness after quenching HRC | 63 HRC |
We are offering 1.2367 Cold Work SS Round Bar to our clients at reasonable price.
Features:
Minimum Order Quantity | 200 Kilogram |
Shape | Round |
Usage/Application | Construction |
Single Piece Length | 3 - 18 Meter |
Technique | Hot Rolled |
Material | Alloy Steel |
Thickness/Diameter | 60 to 1000 mm |
Hardening Degree C | 840 - 900 Deg C |
Hardness HB | Max 240 |
Cooling | Furnace |
Tensile Strength | Corresponding to Hardness 1220 -1390 N/mm2 |
Standard Thickness Available mm | 126 - 458 mm |
Standard Width Available mm | 160 - 610 mm |
Ventura Alloy and Steels Stocks and Supplies Stainless Steel Rounds Bars in India and abroad. DB6 Steel is an extreme pass on steel with high treating resistance and great through-solidifying properties. Its nickel substance has it uncommonly effect safe – a highly recommendable element for vast mallet & press bites the dust alike. This evaluation is generally supplied in toughened condition or extinguished and tempered to 1300 N/mm² & a working hardness of 370 to 410 HB (round) or 355 to 400 HB (square, level).
Utilized as standard steel for manufacturing passes on of different kinds, press bites the dust, expulsion kicks the bucket, retainer plates, heavily clad trim bites the dust, hot shear sharpened pieces of steels and instrument holder.
Utilized as standard steel for manufacturing passes on of different kinds, press bites the dust, expulsion kicks the bucket, retainer plates, heavily clad trim bites the dust, hot shear sharpened pieces of steels and instrument holder.
Utilized as standard steel for manufacturing passes on of different kinds, press bites the dust, expulsion kicks the bucket, retainer plates, heavily clad trim bites the dust, hot shear sharpened pieces of steels and instrument holder.
Process Route:
Eaf+Lf+Vd+Upset+Forged+Annealed+Rough Turned For Rounds/Milled For Flats+Oil Quenched And Double Tempered+ Rough Turned For Rounds/Milled For Flats
Steel Properties:
The special Hot Work Pre-hardened Steel has great toughness and high wear resistance. DB6 Steel is generally supplied in hard, quenched, tempered and also in annealed condition in special cases. Usually it's working hardness is 360-430 BHN. This steel grade is the upgraded version of DIN 2713 for greater efficiency and performance.
Application:
Dies for Specially Drop and Close Die Forgings for Hammers & Mechanical Presses, Die Moulds, Shoe Blocks, Die Holder, Cassettes, Piston Rods, Cranks, Boaster, Shearing Blades, Tools, Plastic Moulds etc.
Minimum Order Quantity | 200 Kilogram |
Shape | Round |
Single Piece Length | 3 - 18 Meter |
Technique | Cold Rolled |
Application | Construction, Automobile Industry |
Thickness/Diameter | 60 to 1000 mm |
Hardness Tolerance | 3 HRC |
Tensile Strength | Corresponding to Hardness 1220 -1390 N/mm2 |
Forging Ratio | 4 1 |
Yield Strength | Corresponding to Tensile 1100 N/mm2 Minimum |
Diameter Tolerance | 0 /+10 mm ( max ) But aim 5 mm |
Standard Width Available mm | 160 - 610 mm |
Standard Thickness Available mm | 126 - 458 mm |
Soft annealing Degree C | 650 - 710 Deg C |
Ventura Alloy and Steels Stocks and Supplies Hot Work Round Bar in India and abroad. DB6 Steel is an extreme pass on steel with high treating resistance and great through-solidifying properties. Its nickel substance has it uncommonly effect safe – a highly recommendable element for vast mallet & press bites the dust alike. This evaluation is generally supplied in toughened condition or extinguished and tempered to 1300 N/mm² & a working hardness of 370 to 410 HB (round) or 355 to 400 HB (square, level).
Utilized as standard steel for manufacturing passes on of different kinds, press bites the dust, expulsion kicks the bucket, retainer plates, heavily clad trim bites the dust, hot shear sharpened pieces of steels and instrument holder.
Utilized as standard steel for manufacturing passes on of different kinds, press bites the dust, expulsion kicks the bucket, retainer plates, heavily clad trim bites the dust, hot shear sharpened pieces of steels and instrument holder.
Process Route:
Eaf+Lf+Vd+Upset+Forged+Annealed+Rough Turned For Rounds/Milled For Flats+Oil Quenched And Double Tempered+ Rough Turned For Rounds/Milled For Flats
Steel Properties:
The special Hot Work Pre-hardened Steel has great toughness and high wear resistance. DB6 Steel is generally supplied in hard, quenched, tempered and also in annealed condition in special cases. Usually it's working hardness is 360-430 BHN. This steel grade is the upgraded version of DIN 2713 for greater efficiency and performance.
Application:
Dies for Specially Drop and Close Die Forgings for Hammers & Mechanical Presses, Die Moulds, Shoe Blocks, Die Holder, Cassettes, Piston Rods, Cranks, Boaster, Shearing Blades, Tools, Plastic Moulds etc.
Minimum Order Quantity | 200 Kilogram |
Single Piece Length | 6 meter |
Technique | Hot Rolled |
Application | Construction |
Shape | Rounds |
Hardness HB | Max 240 |
Hardening Degree C | 840-900 Deg C |
Hardness after quenching HRC | 55-57 HRC |
Cooling | Furnace |
Round | 60 to 1000 mm |
Material | Alloy Steel |
We are offering DB6 Stainless Steel Rods to our clients.
Chemical Composition - (Typical Analysis in %)
STANDARDS | 55NiCrMoV7 | DB6 | DIN 2714 | AISI L6 | AFNOR 55NCDVV7 | JIS SKT4 |
C | Si | Mn | P | S | Cr | Ni | Mo | V |
0.50-0.60 | 0.10-0.40 | 0.65-0.95 | <0.015 | <0.004 | 1.0-1.20 | 1.50-1.80 | 0.45-0.55 | 0.07-0.12 |
USA | Europe | Germany | China | Japan | India | R. of Korea | Russia |
AISI / SAE | En | DIN, WNr | GB | JIS | IS | KS | GOST |
A681 L6 | 55NiCrMoV7 | 56NiCrMoV7 | 5CrNiMo | SKT4 | T55Ni7Cr4Mo5V1 | STF4 | 4ChMNFS |
Ventura Alloy and Steels Stocks and Supplies Die Block Steels DB6 / 2714 in India and abroad. DB6 Steel is an extreme pass on steel with high treating resistance and great through-solidifying properties. Its nickel substance has it uncommonly effect safe – a highly recommendable element for vast mallet & press bites the dust alike. This evaluation is generally supplied in toughened condition or extinguished and tempered to 1300 N/mm² & a working hardness of 370 to 410 HB (round) or 355 to 400 HB (square, level).
Utilized as standard steel for manufacturing passes on of different kinds, press bites the dust, expulsion kicks the bucket, retainer plates, heavily clad trim bites the dust, hot shear sharpened pieces of steels and instrument holder.
Utilized as standard steel for manufacturing passes on of different kinds, press bites the dust, expulsion kicks the bucket, retainer plates, heavily clad trim bites the dust, hot shear sharpened pieces of steels and instrument holder.
Process Route:
Eaf+Lf+Vd+Upset+Forged+Annealed+Rough Turned For Rounds/Milled For Flats+Oil Quenched And Double Tempered+ Rough Turned For Rounds/Milled For Flats
Steel Properties:
The special Hot Work Pre-hardened Steel has great toughness and high wear resistance. DB6 Steel is generally supplied in hard, quenched, tempered and also in annealed condition in special cases. Usually it's working hardness is 360-430 BHN. This steel grade is the upgraded version of DIN 2713 for greater efficiency and performance.
Application:
Dies for Specially Drop and Close Die Forgings for Hammers & Mechanical Presses, Die Moulds, Shoe Blocks, Die Holder, Cassettes, Piston Rods, Cranks, Boaster, Shearing Blades, Tools, Plastic Moulds etc.
Minimum Order Quantity | 200 Kilogram |
Usage/Application | Construction |
Single Piece Length | 6 meter |
Reduction Ratio | Billet size minimum 180 x 180 |
Spark and Spectral | 100% spark & spectral tested Material and free from mix up |
Application | Automobile Industry |
Microstructure | Ferrite and Pearlite |
Gas Content | N2-80PPM max, H2-2PPM max, O2-15PPM max |
Hardness | 350 BHN max |
Diameter | 8 - 32 mm |
Shape | Round |
We are offering 50CRV4 SS Round Bar to our clients.
Chemical Composition - (Typical Analysis in %)
C | Cr | Mn | V | Si | P | S |
0.47-0.55 | 0.80-1.20 | 0.70-1.10 | 0.15min | 0.15-0.40 | 0.30max | 0.30max |
VENTURA EN47 Chromium Vanadium type spring steel supplied in the as rolled condition as well as spheroidized annealed condition. EN47 is suitable for oil hardening and tempering. When used in the oil hardened and tempered condition EN47 spring steel combines spring characteristics with good wear and abrasion resistance. When hardened EN47 offers excellent toughness and shock resistance which make it a suitable alloy spring steel for parts exposed to stress, shock andvibration.
Applications:
En47 steels, highlight the advantage is good hardenability, another hot working performance, comprehensive mechanical properties, decarburization resistance is also good big cross section of various important spring, such as automobile, locomotive, large plate spring, spring, etc. SUP10 Spring main used for heavy vehicles, tractors, industrial production load, stress and the diameter of the larger plate spring and helical spring. It is also used widely in the motor vehicle industry and many general engineering applications. Suitable for applications that require high tensile strength and toughness. Typical applications include crankshafts, steering knuckles, gears, spindles and pumps.
Forging:
Forge at 1050°C. Do not work this steel when it has fallen below 840°C.
Annealing:
Heat slowly to 820-840°C, soak well. Cool slowly in the furnace. (Our annealing is done in electric furnace to avoid decarburization.)
Hardening:
Pre heat slowly to 650/700°C and thoroughly soak. Continue heating to the final hardening temperature of 830/860°C and allow the component to be heated through. Quench in oil.
Tempering:
Temper the EN47 spring steel component immediately after quenching whilst tools are still handwarm. Re-heat to the tempering temperature then soak for one hour per 25 millimetre of total thickness (2 hours minimum) Cool in air. For most applications tempering of this grade will be between 400-600°C.
Heat Treatment:
Heat treatment temperatures, including rate of heating, cooling and soaking times etc. will vary due to factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and workpiece transfer facilities. Please consult your heat treatment provider for full guidance on heat treatment of EN47.
Sizes Available:
20 x 20 mm, 22 x 22 mm, 25 x 25 mm, 25 x 60 mm, 28 x 28 mm, 28 x 36 mm, 32 x 32 mm, 36 x 36 mm, 36 x 45 mm, 55 x 55 mm, 40 x 40 mm, 45 x 45 mm, 45 x 55 mm
Minimum Order Quantity | 200 Kilogram |
Usage/Application | Construction |
Shape | Round |
Single Piece Length | 3 - 18 Meter |
Technique | Cold Rolled |
Thickness/Diameter | 20 to 450 mm |
Coefficient of thermal expansionat Degree C | 20-700 Deg C |
Soft annealing Degree C | 810 -850 Deg C |
Tempering Degree C after Quenching | 100-600 Deg c |
Hardness after quenching HRC | 64.5 HRC |
Quenching | Oil, Air (up to 30 mm thickness) |
Hardening Degree C | 940-980 Deg C |
Steel Properties:
Application:
P20 is equivalent grade of most popular steel grade of DIN 2738 which is applicable for large & small plastic mould dies for Automotive Industries, Dies for Domestic goods , High finishing plastic Die, Bolster Plates of Presses, Die Holders & Shoe blocks for drop Hammers, Press Cassettes , Upsetter Blocker, forging dies, Different dies & mold for plastic products etc.
Physical Properties:
Coefficient of Thermal Expansion at °C | 10¯??? m / (m*K) |
20-100 | 11.2 |
20-200 | 12.8 |
20-300 | 13.5 |
20-400 | 13.7 |
20-500 | 14.3 |
20-600 | 14.7 |
20-700 | 14.9 |
Thermal Conductivity at °C | W / (m*K) |
20 | 35 |
350 | 34 |
700 | 33 |
Heat Treatment:
Soft Annealing °C | 710-740 |
Cooling | Furnace |
Hardness HB | max. 235 |
Hardening °C | 840-870 |
Quenching | Polymer or Oil |
Hardness after quenching HRC | 51 |
Tempering°C after quenching | 100 | 200 | 300 | 400 | 500 | 600 | 700 |
HRC | 51.5 | 50.2 | 48 | 46.2 | 43 | 39 | 29 |
Price Range:
Minimum Order Quantity | 200 Kilogram |
Technique | Cold Rolled |
Application | Automobile Industry, Construction |
Size/Diameter | 20 to 450 mm |
Single Piece Length | 6 meter, 18 meter, 3 meter |
Coefficient of thermal expansion at Degree C | 20-400 Deg c |
Soft annealing Degree C | 840-870 Deg C |
Hardness HB | Max 250 |
Hardening Degree C | 1000-1050 Deg C |
Hardness after quenching HRC | 63 HRC |
Chemical Composition - (Typical Analysis in %)
STANDARDS | X153CrMoV12 | HCHCR-D2 | DIN 2379 | AISI D2 | AFNOR Z160CDV12 | JIS SKD10 |
C | Si | Mn | P | S | Cr | Mo | V |
1.40-1.60 | 0.10-0.60 | 0.20-0.60 | 0.030max | 0.030max | 11.00-13.00 | 0.70-1.00 | 0.80-1.20 |
Ventura Alloy and Steels Supplies and Stocks HCHCR D2 in India and abroad. D2 steel is an air hardening, high-carbon, high-chromium tool steel. It has high wear and abrasion resistant properties. It is heat treatable and will offer a hardness in the range 55-62 HRC, and is machinable in the annealed condition. It tends to be used as threading rolls and dies, icy trimming, cutting & stamping tools for sheet thickness up to 6mm, accuracy cutting instruments for sheet thicknesses up to 12 mm.
Steel Properties:
Application:
HCHCR D2 tool steel can be utilized for cold stamping or forming dies, cold forming rolls, slitters, shear blades, tools, tyre shredders, chipper knives, punches, trimming, cutting threading dies, stamping tools and more.
Physical Properties:
Coefficient of Thermal Expansion at °C | 10-??? m / (m*K) |
20-100 | 10.6 |
20-200 | 11.5 |
20-300 | 11.8 |
20-400 | 12.3 |
Thermal Conductivity at °C | W / (m*K) |
20 | 16.7 |
350 | 20.5 |
700 | 24.2 |
Heat Treatment:
Soft Annealing °C | 840-870 |
Cooling | Furnace |
Hardness HB | max. 250 |
Stress-relief Annealing °C | approx. 660-710 |
Hardening °C | 1000-1050 |
Quenching | Air, Oil, Salt Bath 500-550°C |
Hardness after quenching HRC | 63 |
Tempering°C after quenching | 100 | 200 | 300 | 400 | 500 | 525 | 550 | 600 |
HRC | 64 | 61.5 | 58.5 | 58.5 | 59 | 60 | 57 | 50 |