Minimum Order Quantity | 200 Onwards |
Application | Automobile Industry |
Coefficient of thermal expansion at Degree C | 20-500 Deg C |
Thermal Conductivity at Degree C | 20-700 Deg C |
Soft annealing Degree C | 710 - 740 Deg C |
Cooling | Furnace |
Hardness HB | Max 235 |
Thickness | 20 to 400 mm |
Width | 40 to 700 mm |
Steel Properties:
Application:
P20 is equivalent grade of most popular steel grade of DIN 2738 which is applicable for large & small plastic mould dies for Automotive Industries, Dies for Domestic goods , High finishing plastic Die, Bolster Plates of Presses, Die Holders & Shoe blocks for drop Hammers, Press Cassettes , Upsetter Blocker, forging dies, Different dies & mold for plastic products etc.
Physical Properties:
Coefficient of Thermal Expansion at °C | 10¯⁶ m / (m*K) |
20-100 | 11.2 |
20-200 | 12.8 |
20-300 | 13.5 |
20-400 | 13.7 |
20-500 | 14.3 |
20-600 | 14.7 |
20-700 | 14.9 |
Thermal Conductivity at °C | W / (m*K) |
20 | 35 |
350 | 34 |
700 | 33 |
Heat Treatment:
Soft Annealing °C | 710-740 |
Cooling | Furnace |
Hardness HB | max. 235 |
Hardening °C | 840-870 |
Quenching | Polymer or Oil |
Hardness after quenching HRC | 51 |
Tempering°C after quenching | 100 | 200 | 300 | 400 | 500 | 600 | 700 |
HRC | 51.5 | 50.2 | 48 | 46.2 | 43 | 39 | 29 |
Price Range:
Minimum Order Quantity | 200 Kg |
Application | Automobile Industry |
Shape | Rectangular |
Thickness | 20 - 400 mm |
Soft Annealing | 710 - 740 Deg C |
Hardness HB | Max 235 |
Hardening Degree C | 840 - 870 |
Hardness after quenching HRC | 51 |
Cooling | Furnace |
Coefficient of thermal expansionat Degree C | 20-700 |
Quenching | Polymer or Oil |
Width | 40 - 700 mm |
We are offering 2311 Plastic Mould Steel Block to our clients.
Chemical Composition - (Typical Analysis in %)
STANDARDS | P20+Ni | DIN 2738 | 40CrMnNiMo8-6-4 | AISI P20+Ni |
C | Si | Mn | P | S | Cr | Ni | Mo |
0.35-0.45 | 0.20-0.40 | 1.30-1.60 | 0.030max | 0.030max | 1.80-2.10 | 1.90-1.20 | 0.15-0.35 |
It has excellent hardening penetration and is specially used for Plastic injection die moulds. Hardness in as supplied condition 280-320 HB with having uniform hardness. The additional nickel content of 1 % increases through hardening. It has good machinability, suitable for plastic moulds for medium and big size, Texturing, fine polishability, adequate corrosion resistance, vacuum-degassed steel. It can be subject to a nitriding treatment to improve its wear resistance.
Steel Properties:
Application:
P20 is equivalent grade of most popular steel grade of DIN 2738 which is applicable for large & small plastic mould dies for Automotive Industries, Dies for Domestic goods , High finishing plastic Die, Bolster Plates of Presses, Die Holders & Shoe blocks for drop Hammers, Press Cassettes , Upsetter Blocker, forging dies, Different dies & mold for plastic products etc.
Physical Properties:
Coefficient of Thermal Expansion at °C | 10¯??? m / (m*K) |
20-100 | 11.2 |
20-200 | 12.8 |
20-300 | 13.5 |
20-400 | 13.7 |
20-500 | 14.3 |
20-600 | 14.7 |
20-700 | 14.9 |
Thermal Conductivity at °C | W / (m*K) |
20 | 35 |
350 | 34 |
700 | 33 |
Heat Treatment:
Soft Annealing °C | 710-740 |
Cooling | Furnace |
Hardness HB | max. 235 |
Hardening °C | 840-870 |
Quenching | Polymer or Oil |
Hardness after quenching HRC | 51 |
Tempering°C after quenching | 100 | 200 | 300 | 400 | 500 | 600 | 700 |
HRC | 51.5 | 50.2 | 48 | 46.2 | 43 | 39 | 29 |
Price Range:
Minimum Order Quantity | 200 Onwards |
Application | Automobile Industry |
Thickness | 20 - 400 mm |
Soft Annealing | 710 - 740 Deg C |
Hardness HB | Max 235 |
Hardening Degree C | 840 - 870 |
Hardness after quenching HRC | 51 |
Cooling | Furnace |
Coefficient of thermal expansionat Degree C | 20-700 |
Quenching | Polymer or Oil |
Width | 40 to 700 mm |
We are offering 40CRMNNIMO7 Plastic Mould Steel Block to our clients.
STANDARDS | P20+Ni | DIN 2738 | 40CrMnNiMo8-6-4 | AISI P20+Ni |
Chemical Composition - (Typical Analysis in %)
C | Si | Mn | P | S | Cr | Ni | Mo |
0.35-0.45 | 0.20-0.40 | 1.30-1.60 | 0.030max | 0.030max | 1.80-2.10 | 1.90-1.20 | 0.15-0.35 |
Steel Properties:
Application:
P20 is equivalent grade of most popular steel grade of DIN 2738 which is applicable for large & small plastic mould dies for Automotive Industries, Dies for Domestic goods , High finishing plastic Die, Bolster Plates of Presses, Die Holders & Shoe blocks for drop Hammers, Press Cassettes , Upsetter Blocker, forging dies, Different dies & mold for plastic products etc.
Physical Properties:
Coefficient of Thermal Expansion at °C | 10¯??? m / (m*K) |
20-100 | 11.2 |
20-200 | 12.8 |
20-300 | 13.5 |
20-400 | 13.7 |
20-500 | 14.3 |
20-600 | 14.7 |
20-700 | 14.9 |
Thermal Conductivity at °C | W / (m*K) |
20 | 35 |
350 | 34 |
700 | 33 |
Heat Treatment:
Soft Annealing °C | 710-740 |
Cooling | Furnace |
Hardness HB | max. 235 |
Hardening °C | 840-870 |
Quenching | Polymer or Oil |
Hardness after quenching HRC | 51 |
Tempering°C after quenching | 100 | 200 | 300 | 400 | 500 | 600 | 700 |
HRC | 51.5 | 50.2 | 48 | 46.2 | 43 | 39 | 29 |
Price Range:
Minimum Order Quantity | 200 Kg |
Usage/Application | Automobile Industry |
Grade | 1.2738 |
Shape | Rectangular |
Thickness | 20 to 400 |
Technique | Hot Rolled |
Hardness | 1030-1060 Deg C |
Width | 40 to 700 mm |
STANDARDS | P20+Ni | DIN 2738 | 40CrMnNiMo8-6-4 | AISI P20+Ni |
C | Si | Mn | P | S | Cr | Ni | Mo |
0.35-0.45 | 0.20-0.40 | 1.30-1.60 | 0.030max | 0.030max | 1.80-2.10 | 1.90-1.20 | 0.15-0.35 |
Coefficient of Thermal Expansion at °C | 10¯??? m / (m*K) |
20-100 | 11.2 |
20-200 | 12.8 |
20-300 | 13.5 |
20-400 | 13.7 |
20-500 | 14.3 |
20-600 | 14.7 |
20-700 | 14.9 |
Thermal Conductivity at °C | W / (m*K) |
20 | 35 |
350 | 34 |
700 | 33 |
Soft Annealing °C | 710-740 |
Cooling | Furnace |
Hardness HB | max. 235 |
Hardening °C | 840-870 |
Quenching | Polymer or Oil |
Hardness after quenching HRC | 51 |
Tempering°C after quenching | 100 | 200 | 300 | 400 | 500 | 600 | 700 |
HRC | 51.5 | 50.2 | 48 | 46.2 | 43 | 39 | 29 |
Minimum Order Quantity | 200 Kg |
Quenching | Polymer or Oil |
Soft annealing Degree C | 710 - 740 |
Cooling | Furnace |
Hardening Degree C | 840 - 870 |
Coefficient of thermal expansionat Degree C | 20-700 |
Hardness after quenching HRC | 51 |
Hardness HB | max 235 |
Shape | Rectangular |
Chemical Composition - (Typical Analysis in %)
STANDARDS | P20+Ni | DIN 2738 | 40CrMnNiMo8-6-4 | AISI P20+Ni |
C | Si | Mn | P | S | Cr | Ni | Mo |
0.35-0.45 | 0.20-0.40 | 1.30-1.60 | 0.030max | 0.030max | 1.80-2.10 | 1.90-1.20 | 0.15-0.35 |
It has excellent hardening penetration and is specially used for Plastic injection die moulds. The characteristics of a material are right sharpening, photo-etching properties with high purity and good homogeneity. P20+Ni is upgraded version of plastic mold steel 0f 2311, which normally supply in Pre hardened condition. Hardness in as supplied condition 280-320 HB with having uniform hardness. The additional nickel content of 1 % increases through hardening. It has good machinability, suitable for plastic moulds for medium and big size, Texturing, fine polishability, adequate corrosion resistance, vacuum-degassed steel. It can be subject to a nitriding treatment to improve its wear resistance.
Steel Properties:
P20+Ni is upgrade version of plastic mold steel 0f 2311, which normally supplied in Prehardened condition
Hardness in supplied condition is 280-320 HB
Additional nickel content of 1 % increases through hardening
It is micro-alloyed
Good machinability
Suitable for texturing
Outstanding Polishability
Corrosion resistance
Vacuum-degassed steel with the following excellent features.
Applications:
P20 is equivalent grade of most popular steel grade of DIN 2738 which is applicable for large & small plastic mould dies for Automotive Industries, Dies for Domestic goods , High finishing plastic Die, Bolster Plates of Presses, Die Holders & Shoe blocks for drop Hammers, Press Cassettes , Upsetter Blocker, forging dies, Different dies & mold for plastic products etc.
Physical Properties:
Coefficient of Thermal Expansion at °C | 10¯??? m / (m*K) |
20-100 | 11.2 |
20-200 | 12.8 |
20-300 | 13.5 |
20-400 | 13.7 |
20-500 | 14.3 |
20-600 | 14.7 |
20-700 | 14.9 |
Thermal Conductivity at °C | W / (m*K) |
20 | 35 |
350 | 34 |
700 | 33 |
Heat Treatment:
Soft Annealing °C | 710-740 |
Cooling | Furnace |
Hardness HB | max. 235 |
Hardening °C | 840-870 |
Quenching | Polymer or Oil |
Hardness after quenching HRC | 51 |
Tempering°C after quenching | 100 | 200 | 300 | 400 | 500 | 600 | 700 |
HRC | 51.5 | 50.2 | 48 | 46.2 | 43 | 39 | 29 |
Minimum Order Quantity | 200 Onwards |
Application | Automobile Industry |
Coefficient of thermal expansion at Degree C | 20-700 |
Hardness HB | Max 235 |
Cooling | Furnace |
Soft annealing Degree C | 710 - 740 |
Tempering Degree C after Quenching | 100-700 |
Hardening Degree C | 840 - 870 |
Quenching | Polymer or Oil |
Hardness after quenching HRC | 51 |
We are offering 2738 Plastic Mould Steel Block to our clients.
Chemical Composition - (Typical Analysis in %)
STANDARDS | P20+Ni | DIN 2738 | 40CrMnNiMo8-6-4 | AISI P20+Ni |
C | Si | Mn | P | S | Cr | Ni | Mo |
0.35-0.45 | 0.20-0.40 | 1.30-1.60 | 0.030max | 0.030max | 1.80-2.10 | 1.90-1.20 | 0.15-0.35 |
It has excellent hardening penetration and is specially used for Plastic injection die moulds. P20+Ni is upgraded version of plastic mold steel 0f 2311, which normally supply in Pre hardened condition. Hardness in as supplied condition 280-320 HB with having uniform hardness. It has good machinability, suitable for plastic moulds for medium and big size, Texturing, fine polishability, adequate corrosion resistance, vacuum-degassed steel. It can be subject to a nitriding treatment to improve its wear resistance.
Steel Properties:
Application:
P20 is equivalent grade of most popular steel grade of DIN 2738 which is applicable for large & small plastic mould dies for Automotive Industries, Dies for Domestic goods , High finishing plastic Die, Bolster Plates of Presses, Die Holders & Shoe blocks for drop Hammers, Press Cassettes , Upsetter Blocker, forging dies, Different dies & mold for plastic products etc.
Physical Properties:
Coefficient of Thermal Expansion at °C | 10¯??? m / (m*K) |
20-100 | 11.2 |
20-200 | 12.8 |
20-300 | 13.5 |
20-400 | 13.7 |
20-500 | 14.3 |
20-600 | 14.7 |
20-700 | 14.9 |
Thermal Conductivity at °C | W / (m*K) |
20 | 35 |
350 | 34 |
700 | 33 |
Heat Treatment:
Soft Annealing °C | 710-740 |
Cooling | Furnace |
Hardness HB | max. 235 |
Hardening °C | 840-870 |
Quenching | Polymer or Oil |
Hardness after quenching HRC | 51 |
Tempering°C after quenching | 100 | 200 | 300 | 400 | 500 | 600 | 700 |
HRC | 51.5 | 50.2 | 48 | 46.2 | 43 | 39 | 29 |
Price Range:
Minimum Order Quantity | 200 Onwards |
Application | Construction |
Shape | Rectangular |
Coefficient of thermal expansionat Degree C | 20-700 Deg C |
Soft annealing Degree C | 710 - 740 Deg C |
Tempering Degree C after Quenching | 100-700 Deg C |
Hardening Degree C | 840 - 870 Deg C |
Quenching | Polymer or Oil |
Hardness after quenching HRC | 51 HRC |
Cooling | Furnace |
Hardness HB | Max 235 |
Thickness | 125 to 1000 mm |
We are offering P20 Ni Plastic Mould Steel Block to our clients.
Chemical Composition - (Typical Analysis in %)
STANDARDS | P20+Ni | DIN 2738 | 40CrMnNiMo8-6-4 | AISI P20+Ni |
C | Si | Mn | P | S | Cr | Ni | Mo |
0.35-0.45 | 0.20-0.40 | 1.30-1.60 | 0.030max | 0.030max | 1.80-2.10 | 1.90-1.20 | 0.15-0.35 |
It has excellent hardening penetration and is specially used for Plastic injection die moulds. The characteristics of a material are right sharpening, photo-etching properties with high purity and good homogeneity. P20+Ni is upgraded version of plastic mold steel 0f 2311, which normally supply in Pre hardened condition. Hardness in as supplied condition 280-320 HB with having uniform hardness. It can be subject to a nitriding treatment to improve its wear resistance.
Steel Properties:
Application:
P20 is equivalent grade of most popular steel grade of DIN 2738 which is applicable for large & small plastic mould dies for Automotive Industries, Dies for Domestic goods , High finishing plastic Die, Bolster Plates of Presses, Die Holders & Shoe blocks for drop Hammers, Press Cassettes , Upsetter Blocker, forging dies, Different dies & mold for plastic products etc.
Physical Properties:
Coefficient of Thermal Expansion at °C | 10¯??? m / (m*K) |
20-100 | 11.2 |
20-200 | 12.8 |
20-300 | 13.5 |
20-400 | 13.7 |
20-500 | 14.3 |
20-600 | 14.7 |
20-700 | 14.9 |
Thermal Conductivity at °C | W / (m*K) |
20 | 35 |
350 | 34 |
700 | 33 |
Heat Treatment:
Soft Annealing °C | 710-740 |
Cooling | Furnace |
Hardness HB | max. 235 |
Hardening °C | 840-870 |
Quenching | Polymer or Oil |
Hardness after quenching HRC | 51 |
Tempering°C after quenching | 100 | 200 | 300 | 400 | 500 | 600 | 700 |
HRC | 51.5 | 50.2 | 48 | 46.2 | 43 | 39 | 29 |
Price Range:
Minimum Order Quantity | 200 Onwards |
Application | Automobile Industry |
Shape | Rectangular |
Technique | 20 to 400 |
Soft Annealing | 710 - 740 Deg C |
Hardness HB | Max 235 |
Hardening Degree C | 840 - 870 |
Hardness after quenching HRC | 51 |
Cooling | Furnace |
Coefficient of thermal expansionat Degree C | 20-700 |
Quenching | Polymer or Oil |
Width | 40 to 700 mm |
We are offering 1.2311 Plastic Mould Steel Block to our clients.
Chemical Composition - (Typical Analysis in %)
STANDARDS | P20+Ni | DIN 2738 | 40CrMnNiMo8-6-4 | AISI P20+Ni |
C | Si | Mn | P | S | Cr | Ni | Mo |
0.35-0.45 | 0.20-0.40 | 1.30-1.60 | 0.030max | 0.030max | 1.80-2.10 | 1.90-1.20 | 0.15-0.35 |
It has excellent hardening penetration and is specially used for Plastic injection die moulds. Hardness in as supplied condition 280-320 HB with having uniform hardness. The additional nickel content of 1 % increases through hardening. It has good machinability, suitable for plastic moulds for medium and big size, Texturing, fine polishability, adequate corrosion resistance, vacuum-degassed steel. It can be subject to a nitriding treatment to improve its wear resistance.
Steel Properties:
Application:
P20 is equivalent grade of most popular steel grade of DIN 2738 which is applicable for large & small plastic mould dies for Automotive Industries, Dies for Domestic goods , High finishing plastic Die, Bolster Plates of Presses, Die Holders & Shoe blocks for drop Hammers, Press Cassettes , Upsetter Blocker, forging dies, Different dies & mold for plastic products etc.
Physical Properties:
Coefficient of Thermal Expansion at °C | 10¯??? m / (m*K) |
20-100 | 11.2 |
20-200 | 12.8 |
20-300 | 13.5 |
20-400 | 13.7 |
20-500 | 14.3 |
20-600 | 14.7 |
20-700 | 14.9 |
Thermal Conductivity at °C | W / (m*K) |
20 | 35 |
350 | 34 |
700 | 33 |
Heat Treatment:
Soft Annealing °C | 710-740 |
Cooling | Furnace |
Hardness HB | max. 235 |
Hardening °C | 840-870 |
Quenching | Polymer or Oil |
Hardness after quenching HRC | 51 |
Tempering°C after quenching | 100 | 200 | 300 | 400 | 500 | 600 | 700 |
HRC | 51.5 | 50.2 | 48 | 46.2 | 43 | 39 | 29 |
Price Range:
Minimum Order Quantity | 200 Kilogram |
Usage/Application | Automobile Industry |
Surface Finish | Polish |
Soft Annealing | 710-740 Deg C |
Hardness | max. 235 HB |
Cooling | Furnace |
Hardening | 840-870 Deg C |
Quenching | Polymer or Oil |
Hardness After Quenching | 51 HRC |
STANDARDS | P20+Ni | DIN 2738 | 40CrMnNiMo8-6-4 | AISI P20+Ni |
C | Si | Mn | P | S | Cr | Ni | Mo |
0.35-0.45 | 0.20-0.40 | 1.30-1.60 | 0.030max | 0.030max | 1.80-2.10 | 1.90-1.20 | 0.15-0.35 |
Coefficient of Thermal Expansion at °C | 10¯??? m / (m*K) |
20-100 | 11.2 |
20-200 | 12.8 |
20-300 | 13.5 |
20-400 | 13.7 |
20-500 | 14.3 |
20-600 | 14.7 |
20-700 | 14.9 |
Thermal Conductivity at °C | W / (m*K) |
20 | 35 |
350 | 34 |
700 | 33 |
Tempering°C after quenching | 100 | 200 | 300 | 400 | 500 | 600 | 700 |
HRC | 51.5 | 50.2 | 48 | 46.2 | 43 | 39 | 29 |