Steel Plates
Leading Wholesale Trader of 2365 hot work steel bars from Mumbai.
2365 Hot Work Steel Bars
₹ 350 / Kg Get Latest Price
| Usage/Application | Automobile Industry |
| Length | 3 - 18 Meter |
| Hardness HB | Max 185 |
| Hardening Degree C | 1040-1060 Deg C |
| Hardness after quenching HRC | 52 HRC |
| Cooling | Furnace |
| Soft annealing Degree C | 740 - 800 Deg C |
| Coefficient of thermal expansionat Degree C | 20 - 700 Deg C |
| Quenching | Oil or Hot Bath 500-550 Degree C |
| Diameter | 50 - 500 mm |
Minimum order quantity: 200 Kg
We are offering 2365 Hot Work Stainless Steel Barsto our clients.
Chemical Composition - (Typical Analysis in %)
STANDARDS | X210CrW12 | H10 | DIN 2365 | AISI H10 | AFNOR 32CDV12-28 |
C | Si | Mn | P | S | Cr | Mo | V |
0.28-0.35 | 0.10-0.400000 | 0.20-0.40 | 0.003 max | 0.030max | 2.70-3.20 | 2.50-3.00 | 0.40-0.75 |
USA | Germany | Japan | British |
AISI / SAE | DIN, WNr | JIS G4404 | BS 4659 |
H10 / T20810 | 1.2365 / 32CrMoV12-28 | SKD7 | BH10 |
Ventura Alloy and Steels Supplies & Stocks H10 Steel in India and abroad. H10 is an amazing high-temperature quality and treating resistance, thermal conductivity and low powerlessness to hot cracking. Utilized for press and penetrating mandrels pass on supplements, massive metal die casting tools.
Steel Properties
- Hot Work Steel H10 is equivalent steel of DIN 2365
- Great tempering resistance
- Less susceptible for high hot cracking
- Excellent thermal conductivity
- High-temperature durability
- Can be water-cooled to a constrained degree
Application:
This tool steel is used for hot press and mandrels, press dieinserts and forging die, remarkable hot metal die casting tools, die-casting moulds for non-ferrous overwhelming metal pressure die-casting.
Physical Properties:
Coefficient of Thermal Expansion at °C | 10¯??? m / (m*K) |
20-100 | 11.7 |
20-200 | 12.4 |
20-300 | 12.7 |
20-400 | 13.2 |
20-500 | 13.5 |
20-600 | 13.7 |
20-700 | 13.8 |
Thermal Conductivity at °C | W / (m*K) |
20 | 32.6 |
350 | 34.4 |
700 | 32.4 |
Heat Treatment:
Soft Annealing °C | 740-800 |
Cooling | Furnace |
Hardness HB | max. 185 |
Hardening °C | 1040-1060 |
Quenching | Oil or Hot Bath 500-550°C |
Hardness after quenching HRC | 52 |
Tempering°C after quenching | 100 | 210 | 300 | 400 | 500 | 550 | 600 | 650 | 700 |
HRC | 51 | 50.5 | 50 | 50 | 53 | 51 | 48 | 41 | 34 |
Contact Us
Aashish Shah (Chairman & Managing Director)
Ventura Alloy And Steels Private Limited
1201 / 1202, Ghanshyam Enclave Premises Co. OP Soc Ltd, Plot No 856, Survey No 33, New Link Road, Kandivali West
Mumbai - 400067, Maharashtra, India