|Minimum Order Quantity||200 Kilogram|
|Soft annealing Degree C||650-710|
|Coefficient of thermal expansion at Degree C||20-700|
|Hardness HB||Max 240|
|Hardening Degree C||1030 - 1060|
|Thermal Conductivity Degree C||20-700|
|Hardness after quenching HRC||55|
We are offering 4Cr5MoSiV1 Hot Work Tool Steel
to our clients.Chemical Composition - (Typical Analysis in %)
|STANDARDS||X40CrMoV5||H13||DIN 2344||AISI H13||AFNOR Z40CDV5||JIS SKD61|
Ventura Alloy and Steels supplies and stocks H13 tool steel in flat, square and round bar. We provide steel in all sizes as your requirements. Consult our team who will assist you for any query related to H13 steel.
SAE AISI H13 steel equivalent with JIS SKD61, GB 4Cr5MoSiV1 and DIN 1.2344 Tool Steel. AISI H13 steel consists of chromium, molybdenum and vanadium and is known for its high hardenability and great toughness.
The molybdenum and vanadium act as strengthening agents while the chromium content helps the AISI H-13 tool steel to withstand softening when used at high temperatures. It also combines shock and abrasion resistance, has good red hardness, can resist rapid cooling and withstand premature heat checking.
H13 Tool Steel has high hot-wear resistance abilities along with great strength, heat conductivity and invulnerability to hot cracking. It has high-temperature strength and resistance to thermal fatigue, glorious through-hardening properties and shows very limited distortion during hardening. H3 ESR is the most purified material with the conventional VD route. The nature of material increase the strength, exceptionally increase the micro-cleanness level. H13 ESR is most refined, has greater homogeneity and an exceptionally fine structure, resulting in improved machinability, polishing & high temperature tensile strength. Exceptionally suggest the use of AISI-H13 ESR grade for Aluminum Pressure Die Casting and other part subjected to high working temperatures and high weight quality. H13 is completely ultrasonic examined with 100% positive outcomes according to NDT standards. Steel Properties:
· Great toughness· Thermal conductivity· High hot-wear resistance· Insusceptible for hot cracking (Hot Crack resistant)· Can be water-cooled to a restricted degree· High Hardenability Application:
This steel is especially used for ejector pins, tool holders and shrink work chucks. It is majorly widely utilized for manufacture of hot forging die & inserts, hot gripper dies, hot nut tools, hot header dies, brass forging and pressing dies, hot forging aluminum base dies, aluminum casting and extrusion dies, zinc die casting dies, extrusion mandrels, cores, die holder blocks, hot press dies, hot work punches, etc. Size Range:
ROUNDS - 10 to 500 MM DIAFLATS - Thickness - 20 to 400 MM MAX | Width - 40 to 700 MM MAXPrice Range:
Rs.150 to 230 per Kg Stocking Partners:
We keep the materials from Germany and China.